ساخت، مشخصه‌یابی و ارزیابی فعالیت زیستی نانوبیوسرامیک فورستریت
نویسندگان
چکیده مقاله:
In this study, forsterite nanopowder was prepared by mechanical alloying and post-heat treatment method. Bioactive properties of forsterite nanopowder were studied by immersing the powder in the SBF. Nanostructure forsterite bulk dense form was prepared by the two step sintering method. It was found that pure forsterite nanopowder with 25-60nm particle size was produced. The results of soaking of forsterite nanopowder in the SBF showed that forsterite nanopowder is bioactive. Also, forsterite dense bulk with the optimal hardness of 940 Hv and fracture toughness of 3.61 MPa.m1/2 was produced. These findings suggest that forsterite nanostructure ceramics possess good biocompatibility, bioactivity and mechanical properties and could be suitable for orthopedic and dental implant materials.
منابع مشابه
ساخت، مشخصه یابی و ارزیابی فعالیت زیستی نانوبیوسرامیک فورستریت
در این تحقیق، نانوپودر فورستریت با استفاده از روش آلیاژ سازی مکانیکی و عملیات حرارتی بعدی ساخته شد. ارزیابی فعالیت زیستی پودر حاصله، در محلول شبیه سازی شده بدن انجام شد. قطعه چگال فورستریت نانومتری با استفاده از فرایند تف جوشی دو مرحله ای ساخته شد. نتایج نشان می دهد که نانوپودر فورستریت با اندازه ذرات 25-60 نانومتر ایجاد شد. بعد از غوطه وری در محلول شبیه سازی شده بدن، رشد فاز آپاتیت در سطح مشاه...
متن کاملساخت و مشخصه‌یابی نانوبیوسرامیک نوین ویلمایت برای ترمیم نواقص استخوانی
The positive effect of Si and Zn ions on bone formation and metabolism has already been confirmed. The aim of this study was preparation and characterization of Willemite (Zn2SiO4) for the repair of bone defects. Willemite was prepared through solid state reaction. Phase analysis and chemical compositions were investigated. The zeta potential of the nanoparticles was determined in physiological...
متن کاملساخت و مشخصه یابی نانوکامپوزیت گلاس آینومر- فورستریت و بررسی تأثیر میزان نانوذرات فورستریت بر خواص مکانیکی و زیست فعالی آن
The objective of this study was to synthesize glass ionomer–forsterite nanocomposite and study the effect of incorporating forsterite nanoparticles to the ceramic part of glass ionomer cement in order to improve mechanical properties and bioactivity. So, Forsterite nanoparticles were made by the sol-gel process using different weight percentages added to the ceramic part of commercial GIC (F...
متن کاملتولید، مشخصه یابی و ارزیابی خواص مکانیکی نانوکامپوزیت آلیاژ پایه کبالت با تقویت کننده نانوپودر فورستریت
Short life of current total hip replacement metallic implants is generally dependent on the aseptic loosening of the implant, which occurs due to mismatch of elastic modulus between bone and metallic implant materials. Decreasing in elasticmodulus of implant could be successful. Forsterite is biocompatible and bioactive ceramic which has suitable mechanical properties. In presented research the...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 29 شماره 1
صفحات 45- 55
تاریخ انتشار 2010-06
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023