بررسی عوامل مؤثر بر سنتز کامپوزیت مولایت-زیرکونیای شکل داده شده توسط فرایند ریخته گری ژلی

نویسندگان

حسین سرپولکی, علم و صنعت ایران

حسین قصاعی, علم و صنعت ایران

نصیبه میعادی, دانشگاه علم و صنعت ایران

چکیده مقاله:

In this study, mullite– irconia composite samples were prepared by reaction sintering of alumina and zircon powder via gel casting process. Gel casting is a new ceramic forming technique. This process is based on the casting of slurry, containing ceramic powder, dispersant and premix monomer solution. To achieve stabilized, high solid loading (80 wt%) and castable slurry, the rheological properties of slurry were optimized. The monomers polymerized the slurry to form gelled specimens. After gelation, the specimens were unmolded, then dried out under controlled condition. Burning out and sintering of the specimens was carried out in the range of 1400-1700°C. Apparent porosity and bulk density of the sintered samples were measured by soaking in water. Crystalline phase evolution and microstructure were determined by XRD and SEM techniques. Results showed that the reaction sintering and mullite formation was completed at 1700°C due to very slow diffusion of Al3+ ions within amorphous silica formed at the decomposition of zircon. The sintered samples at this temperature also showed the lowest apparent porosity (≈ 4%) and the highest bulk density (≈3.40 gr/cm-3).

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

اصلاحیه: بررسی اثر افزودن ایتریا بر خواص کامپوزیت های مولایت -زیرکونیا ساخته شده به روش ریخته گری دوغابی

In this study, the effect of different amounts of Y2O3 on the properties of mullite-zirconia composites was investigated. For this purpose, these composites were fabricated by reaction-sintering of alumina and zircon as raw materials. Besides, the slip casting method was used for forming these composites, and sintering process was carried out at 1600 °C. Then, the physical and mechanical pro...

متن کامل

بررسی عوامل موثر بر ساخت قطعات سیلیس ذوبی به روش ریخته گری ژلی

In this research according to unique properties of fused silica and Its numerous applications fused silica parts with 77% by weight solid loading formed by gel casting. Rheological behavior of the slurry and sintering conditions were optimized. Sample sintered at optimum conditions has bulk density of 1.71 g/cm3, open porosity of 18.13%, water absorption of 10.60%, linear shrinkage after firi...

متن کامل

ریخته گری ژلی نیترید سیلیسیم

این پژوهش با هدف ساخت بدنه های نیترید سیلیسیمی(si3n4) به روش ریخته گری ژلی و بررسی عوامل موثر بر فرآیند انجام شد. دراین تحقیق دوغاب هایی با 70 درصد بار جامد از پودر نیترید سیلیسیم با دانه بندی کمتر از 3/0 میکرون و سیستم مونومری am-mbam با مقادیر مختلف تهیه شدند. در ادامه این دوغاب ها با افزودن کاتالیزور و آغازگر تحت عملیات ریخته گری در قالب پلیمری قرار گرفتند. قطعات پس از خروج از قالب خشک و سپس...

متن کامل