بررسی تاثیر ریزساختار HTPB بر کهولت پیشرانه جامد مرکب با استفاده از آزمون دینامیکی مکانیکی
نویسندگان
چکیده مقاله:
In this article aging behavior of composite solid propellant was investigated by determining its mechanical properties at elevated temperatures. For this purpose, three HTPB samples with different microstructures were selected and composite solid propellants were prepared based on them keeping similar other components and aging was studied by accelerated method. Mechanical properties were measured after accelerated aging using dynamic mechanical thermal analysis (DMTA) in order to investigate the effect of HTPB microstructure on composite solid propellant aging. Results showed that with increasing molecular weight, hydroxyl value, increasing vinyl and decreasing cis contents in resin microstructure, the mechanical behavior of the propellant becomes more rigid, which may be due to limiting the polymer chain mobility or facilitating post-curing crosslinking. Over aging time, the shelf life changed effectively with propellant binder microstructure. The obtained shelf life for the composite solid propellants based on D01, D02 and D03 resin samples were 6, 4.48 and 3.56 years. The results showed significant differences and show well the affect of the micro-structural properties of HTPB resin on the aging of its-based composite solid propellant.
منابع مشابه
بررسی کهولت پیشرانه‌های جامد مرکب برپایه HTPB
کهولت پیشرانه‌های جامد مرکب برپایه‌ی HTPB بررسی می‌شود که یکی از پارامترهای اصلی در ارزیابی طول‌عمر پیشرانه‌های مورد استفاده در سامانه‌های راکتی و موشکی به‌شمار می‌آید. امروزه پیشرانه‌های جامد مرکب بر پایه‌ی HTPB کارآمدترین پیشرانه برای کاربرد در موتورهای پیشرانه جامد در سراسر جهان هستند. فرایندهای کهولت پیشرانه‌های جامد مرکب می‌تواند پیامد فرایندهای شیمیایی، فیزیکی و مکانیکی باشد. در این مقال...
متن کاملبررسی پارامترهای موثر بر کهولت پیشرانه های جامد مرکب بر پایه ی htpb
پیشرانه های جامد مرکب بر پایه ی htpb منبع انرژی برای پیشرانش راکت ها و موشک ها می باشند. از آنجایی که پیشرانه های جامد مورد استفاده در سامانه های راکتی و موشکی با سرعت بیشتری نسبت به دیگر اجزای سیستم دچار تخریب می شوند لذا طول عمر کل سیستم عمدتاً به وسیله ی عمر پیشرانه ها تعیین می شود. گرین های پیشرانه در موقع انبارداری و حمل و نقل در معرض عوامل محیطی مختلفی همچون رطوبت، دما، ارتعاش و شوک قرار ...
متن کاملبررسی کهولت پیشرانه‌ی جامد مرکب بر پایه‌ی HTPB با استفاده از روش وان‌هوف
In this article the aging of HTPB based composite solid propellants have been studied by Van’t Hoff method. The F-factor of Van’t Hoff equation was calculated by dynamic mechanical analysis (DMA) for reference propellants sample that was equal 2.5. Then the accelerated aging program conditions have been determined by Van’t Hoff equation. According to accelerated aging program the reference prop...
متن کاملاثر مقدار دی‌مریل دی‌ایزوسیانات بر رفتاررئولوژیکی و خواص مکانیکی یک پیشرانه جامد مرکب بر پایه HTPB
Several parameters affecting the rheological and mechanical properties of solid composite propellants. Among them, the molar ratio of isocyanate (NCO) to hydroxyl (OH) groups (R value) is one of the important factors. In this research, the effects of changing in the weight ratio of dimeryl diisocyanate (DDI) curing agent related to hydroxyl terminated polybutadiene investigated on different pr...
متن کاملمطالعه پارامترهای موثر بر خواص مکانیکی پیشرانه جامد مرکب بر پایه HTPB/Al/AP
The success of the composite solid propellant motor depends on the proper stress-strain behavior of the propellant grain against tensile, compression and shear stresses and intensive changes in gravity during launch. In this paper, the effect of formulation components and other parameters affecting mechanical properties (tensile strength, elongation and elastic modulus), and their effects AP/Al...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 16 شماره 1
صفحات 3- 12
تاریخ انتشار 2021-03
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023