In this paper the effect of ammonium hydroxide addition to the solution of metallic oxide on sol gel preparation process of YBCO is studied with differential thermal analysis, thermal graviometry and X-ray diffraction. Two samples with and without ammonium hydroxide. Ammonium hydroxide prevents both barium nitrate precipitate during the gel preparation and also unwanted reaction as well as increasing homogeneous product. After drying the gel, the samples heated up to 1050°C in DTA apparatus in order to find more accurate the type and the temperature of reaction during the preparation process. After the initial reactions in the samples, Y2Cu2O5 and 123 phases are created in the range of 780-840°C and then the 123 phase is strengthened at 900-950°C. As shown in X-ray data, 123 was the only phase after this range. In addition ammonium hydroxide support and increase the creation of 123 phase at lower temperature.
منابع مشابه
اثر هیدراکسید آمونیوم بر فرآیند ساخت ابررسانای yba<sub>۲</sub>cu<sub>۳</sub>o<sub>۷-x </sub> به روش سل- ژل
در این مقاله با استفاده از بررسیهای آنالیز حرارتی تفاضلی، وزن سنجی حرارتی وپراش اشعه x (xrd) ، اثر افزودن هیدراکسید آمونیوم به محلول نمک نیترات فلزات در مراحل ساخت ابررسانای سرامیکی ybco به روش سل- ژل مورد بررسی قرار می گیرد. دو نوع نمونه یکی بدون هیدراکسیدآمونیوم و دیگری با هیدراکسید آمونیوم تهیه گردید. افزایش هیدراکسیدآمونیوم از ایجاد رسوب نیترات باریوم در هنگام تشکیل ژل جلوگیری می کند و از ب...
متن کاملمطالعه ابررسانای Bi1.64Pb0.36Sr2Ca2-xCdxCu3O10ساخته شده به روش سل ـ ژل
چکیده ابررسانای سرامیکی Bi1.64Pb0.36Sr2Ca2-xCdxCu3O10آلایش یافته با Cd به روش سل ـ ژل ساخته شد. برای تهیه نمونهها، مقدار آلایش کادمیوم از 2/0-0=x و زمانهای پخت 32، 48، 56 و 64 ساعت انتخاب شدند. برای یافتن دمای شروع واکنش مواد اولیه از ژل خشک شده آنالیز TGA گرفته شد. ریختشناسی و ریزساختار نمونهها توسط XRD و SEM مورد بررسی قرار گرفت. نتایج حاصل از XRD نشان داد که بیشترین درصد فاز 2223-Bi ،ب...
متن کاملبررسی ابررسانای Bi1.6Pb0.4Sr2-xBaxCa2Cu3Oy ساخته شده به روش سل- ژل
In this study, the effect of Ba substitution for Sr in the Bi-Pb-Sr-Ca-Cu-O (BPSCCO) system was investigated. The Bi1.6Pb0.4Sr2-xBaxCa2Cu3Oy superconductor with 0.0, 0.05, 0.1, 0.15, 0.2, 0.25 and 0.3 at annealing times of 16, 32, 48 and 64 hour was made by the sol-gel method. In order to study the microstructure of samples, SEM images and X-ray diffraction (XRD) was performed. The crystal la...
متن کاملساخت نانو ذرات ابررسانای YBCO به روش ترکیبی سل- ژل، خود احتراقی
This paper describes the details of synthesizing nano crystalline YBCO superconductor using a sol-gel combustion method and the effect of sol pH and sintering temperature on particle size was investigated. The sintering temperature was chosen 880°C and the samples were annealed at this temperature for 5 hours. The morphology and structure of the nano scale products were characterized by powder ...
متن کاملساخت ابررسانای yba2cu3o7 به روش سل-ژل و بررسی اثر ناخالصی er2o3 بر دمای گذار این ترکیب
چکیده ندارد.
15 صفحه اولاثر آلایش Ni و Fe در ترکیب ابررسانای YBCO ساخته شده به روش سل ـ ژل
We fabricated YBa2Cu3-xMxO7- d (M=Ni, Fe) bulk samples, with stochiometric amount 0≤x≤0.045 by sol-gel method. The phase analysis and microstructure of specimens were examined by XRD and SEM. The electrical resistivity was measured using standard four probe technique for 77-300K. Investigation of XRD spectrum by MAUD shows Ni and Fe ions substitute in Cu(2) and Cu(1) site, respectively. Transi...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 6 شماره 3
صفحات 215- 219
تاریخ انتشار 2006-09
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023