Mashhadi, M.
2. Department of Composite Materials Engineering, Malek Ashtar University of Technology, Tehran, Iran.
[ 1 ] - Synthesis of HfB2 Powders by Carbothermal Reduction
In this research, solid state carbothermal synthesis of HfB2 Nano powders was investigated. For this purpose, HfO2,H3BO3, carbon active or phenolic resin were used as raw materials for carbothermal reaction. After 2-4 hours of milling the raw materials by a planetary ball in an ethanol media, the mixture was heat dried and pressed in to disks under pressure of 20-30 bar. The disks were then pla...
[ 2 ] - Synthesis of Boron Nitride powder by carbothermal method, using phenolic resin and carbon black and investigating the effect of additive of calcium carbonate
Effect of CaCO3 on carbothermic formation of hexagonal boron nitride (h-BN) was investigated. B2O3–C mixtures containing CaCO3 additive were reacted at 1500 for 120 min in nitrogen atmosphere. Formed phases in the reaction products were determined by powder-XRD analyses, and amounts of the constituents were determined by chemical analyses. Particle size and morphology of the formed h-BN powde...
[ 3 ] - بررسی خواص فیزیکی، مکانیکی و مقاومت به اکسیداسیون نانوکامپوزیت ZrC-ZrB2-SiC تقویت شده با الیاف کربنی
This article has no abstract.
[ 4 ] - Fabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
[ 5 ] - review of the mechanical and thermal properties of high temperature Diboride ceramics
Ceramic borides, carbides and nitrides with high melting point, relatively good resistance to oxidation and corrosive environments are considered by many researchers in various high temperature industries, which is known from the family of materials as high temperature ceramic (UHTC). To be. All UHTCs have very strong bonds that give them structural stability at high temperatures, and among the...
Co-Authors