[ 1 ] - Tribological behavior of sputter-deposited MoSX/Ni coatings
AbstractSputtered MoS2 coatings have been mostly used as a solid lubricant. In this investigation, MoSx/Ni composite coatings with Ni contents varying from 0 to 22 % were deposited onto steel substrate using a DC magnetron sputter process. The MoS2/Ni ratio in the coatings was controlled by sputtering the composite targets. The composition, microstructure, and mechanical properties of the...
[ 2 ] - A Study of the Tribological Properties of Sputter-deposited MoSX/Cr Coatings
In this investigation, MoSx/Cr coatings were deposited by direct-current magnetron sputter onto Ck45 (AISI 1045) plain carbon steel substrates. The MoSx/Cr ratio in the coatings was controlled by sputtering the composite targets. The chemical characterization was performed using EDX (energy dispersive X-ray analysis); the structural characterization was accomplished by X-ray diffraction (XRD) s...
[ 3 ] - بررسی خواص پوشش MoS2-Ti ایجاد شده توسط فرآیند پراکنش مگنترونی DC
دی سولفید مولیبدن (MoS2) یکی از رایج‌ترین پوشش‌های روانکار جامد است که تاکنون با استفاده از روش‌های مختلفی، روی سطوح تحت سایش اعمال‌شده است. این پوشش به علت حساسیت بالا به رطوبت کارایی مناسبی در شرایط محیطی ندارد. یک روش برای کاهش حساسیت آن به رطوبت و اکسیژن هم رسوبی MoS2 با عناصر است. در این تحقیق پوشش‌های MoSx/Ti- به روش کندوپاش مغناطیسی جریان مستقیم، روی فولاد اعمال شد. نسبت تیتانیوم در پوشش...