[ 1 ] - Preparation of nano silver powder from acid leaching tail in gold room

According to the unique properties and many applications of nano silver powder, it was prepared from acid leaching tail solution. The low value residual gold and silver ions were occurred with fellow heavy metals as pollutants (Fe2+, Cu 2+ and Zn2+) in acid leaching tail solution in Mouteh gold mine in Iran. Preparation of nano silver particles was achieved in two steps: first, by addition of a...

[ 2 ] - Preparation of nano gold powder from acid leaching tail solution

According to the unique properties and many applications of nano gold powder, it was prepared from an acid leaching tail solution. The low value residual gold ions existed in acid leaching tail solution in Mouteh gold mine in Iran with fellow heavy metals as pollutants (Fe2+, Cu2+, and Zn2+). Preparation of nano gold particles is achieved by two steps: First, by addition of ammonia as separatio...

[ 3 ] - Aliphatic alcohols oxidation with Hydrogen Peroxide in water catalyzed by supported Phosphotungstic acid (PTA) on Silica coated MgAl2O4 nanoparticles as a recoverable catalyst

In this paper, a novel catalyst (MgAl2O4@SiO2-PTA) was proposed for the green oxidation of aliphatic alcohols. The resultant composite was characterized by different techniques, such as X-ray diffraction (XRD), SEM, FT-IR, EDX and Brunauer-Emmett-Teller (BET) surface area analysis. The prepared nanocomposite was used as a catalyst for oxidation of aliphatic alco...

[ 4 ] - Aliphatic alcohols oxidation with Hydrogen Peroxide in water catalyzed by supported Phosphotungstic acid (PTA) on Silica coated MgAl2O4 nanoparticles as a recoverable catalyst

In this paper, a novel catalyst (MgAl2O4@SiO2-PTA) was proposed for the green oxidation of aliphatic alcohols. The resultant composite was characterized by different techniques, such as X-ray diffraction (XRD), SEM, FT-IR, EDX and Brunauer-Emmett-Teller (BET) surface area analysis. The prepared nanocomposite was used as a catalyst for oxidation of aliphatic alco...

[ 5 ] - Preparation of nano silver powder from acid leaching tail in gold room

According to the unique properties and many applications of nano silver powder, it was prepared from acid leaching tail solution. The low value residual gold and silver ions were occurred with fellow heavy metals as pollutants (Fe2+, Cu 2+ and Zn2+) in acid leaching tail solution in Mouteh gold mine in Iran. Preparation of nano silver particles was achieved in two steps: first, by addition of a...

[ 6 ] - Preparation of nano gold powder from acid leaching tail solution

According to the unique properties and many applications of nano gold powder, it was prepared from an acid leaching tail solution. The low value residual gold ions existed in acid leaching tail solution in Mouteh gold mine in Iran with fellow heavy metals as pollutants (Fe2+, Cu2+, and Zn2+). Preparation of nano gold particles is achieved by two steps: First, by addition of ammonia as separatio...

[ 7 ] - Characterization of Structural, Optical and Hydrophilicity properties of TiO2 Nano-Powder Synthesized by Sol-Gel Method

In this paper, titanium dioxide nano-particles were synthesized by sol-gel method in acidic atmosphere. The microstructure, morphology, optical band gap, and hydrophilicity of the sample were studied. Optical band gap of titanium dioxide was probed via Diffuse Reflectance Spectra (DRS) and contact angle (CA) was measured to investigate surface activity. XRD analysis was used to study crys...

[ 8 ] - Synthesis and characterization of Mg1-xNixAl2O4 and their photocatalytic behaviors towards Congo red under UV light irradiation

In this paper, MgAl2O4 nanoparticles were synthesized by the Sol-gel auto combustion method and were doped with different concentrations of Ni2+ (x= 0, 0.1, 0.05, and 0.03). By this method, a novel photocatalyst which had better decolorization percentages of Congo redcompared to MgAl2O4 was produced. The MgAl2O4 sample...