[ 1 ] - تولید و مشخصه یابی کامپوزیت نانوساختار Al-Mg-Zn/ 3 wt.% Al2O3 بوسیله زمینه پیش آسیاب شده توسط آلیاژسازی مکانیکی
Al-Zn-Mg/3 wt-% Al2O3 nanostructured composite powder was synthesized through Mechanical Alloying (MA). At first, the 7014 alloy matrix constituents were milled in a planetary ball mill for 20 hours. Then, 3 wt.% µ-Al2O3 particles were added to the pre-milled matrix and the nanostructured composite powder was produced at different MA times to investigate the effects of MA time ...
[ 2 ] - Creep Life Assessment of Primary Reformer HP40-NB Modified Steel Tube of an Ammonia Plant
Assessment of creep damage and residual creep life of a cast HP 40 Nb Mod. Reformer tube was performed, wherein the experimental Larson–Miller diagram and area fraction of creep voids were adopted. The state of damage of the tube in service was metallographically analyzed by using light and electron microscopy. Samples from the serviced reformer furnace tube were cut and prepared for void exami...
[ 3 ] - Strengthening Mechanisms in the Aged 2024 and 7075 Aluminium Alloys
Aluminum 2024 and 7075 alloys which are widely used in aerospace and marine applications were chosen to investigate their strengthening mechanisms. Using differential thermal analysis (DIA), metallography and tension tests, the best solutionizing conditions were determined to be 500±5°C and 2 hours for 2024 and 480?±5°C and 1 hour for 7075 alloy. Aging was performed in the range of 100 to 200°C...