[ 1 ] - پوشش دو لایه HA/TiO2 بر روی زیرلایه Ti-6Al-4V به روش کند و پاش مگنترون RF
در تحقیق حاضر، لایه‌هایی از HA ، TiO2 و HA/TiO2 با روش کند و پاش مگنترون AC و DC بر روی زیرلایه Ti-6Al-4V پوشش داده شدند. در این جا با تعیین پارامترهای بهینه پوشش‌دهی که برای هیدروکسی آپاتیت توان W 175 و برای تک لایه تیتانیا نسبت آرگون به اکسیژن (Ar/O2) 70/30 بود، نمونه دو لایه HA/TiO2 پوشش‌دهی گردید. به منظور بررسی فازهای تشکیل شده، مورفولوژی و زبری سطح به ترتیب از پراش اشعه ایکس (XRD)، میکروس...
[ 2 ] - رفتار سیلان آلیاژ Ti-6AL-4V تجاری با ریز ساختار لایه‌ای در فورج همدما
In this paper, plastic flow behavior and micro structural evolution of Ti-6Al-4V alloy in temperature range of 750-1050 °C and strain rate range of 0.001-0.1 (S-1) in isotherm compression condition were investigated. The purpose was to estimate activation energy of globularization of lamellar structure and analyze this process kinetically. True Stress-strain curves obtained at the temperat...
[ 3 ] - On the Characteristics of Friction Stir Welding Lap Joint of Magnesium and Aluminum
Lap joints of commercially pure magnesium plates to aluminium plates (Magnesium plate on the top, and Aluminium plate, grade 1100, on the bottom side) were conducted by friction stir welding using various traveling and rotation speeds of the tool to investigate the effects of the welding parameters on the joint characteristics and strength. Defect-free lap joints were obtained in the welding tr...
[ 4 ] - SURFACE HARDENING OF TUNGSTEN-BASED HEAVY ALLOY VIA PACK BORONIZING
The boronizing of a tungsten heavy alloy containing Ni and Fe as the major alloying elements were performed in the present study to increase its surface hardening. Pack cementation method was employed as a well-known, successful solid-state process for boronizing. The coating treatment was accomplished at different temperatures of 1000, 1050 and 1100°C for 6 and 9 hours. The formation of tu...
[ 5 ] - مقایسه خواص مکانیکی و متالورژیکی کامپوزیت میکروساختار و نانوساختار WC-9Co-0.7VC
کامپوزیت‌های WC-Co که به هاردمتال‌ها موسوم اند، استفاده گسترده ای در بخش صنعت حفاری نفت و گاز دارند. چند سالی است که استفاده از این کامپوزیت ها با ساختار نانو، مورد توجه قرار گرفته است. در این تحقیق، کامپوزیت WC-9Co-0.7VC در دو حالت میکروساختار و نانوساختار با استفاده از فرآیند پرس داغ سریع ساخته شده و سپس ریزساختار و خواص مکانیکی آن‌ها با یکدیگر مقایسه شده است. خواص مکانیکی کامپوزیتِ هاردمتالِ...
[ 6 ] - Convectional hydrothermal synthesis of high-purity pesudo-cubic BaTi0.09Nb0.01O3 nanocrystals in rotary autoclave
Nano-sized BaTiO3 powders with particular Nb concentrations were prepared by Rotary- Hydrothermal (RH) method. Hydrothermal method was used at 180 °C for 5 hours with new Ti pressure and the teflon vessel was rotated at a speed of 160 rpm during the hydrothermal reaction. New hydrothermal method was used instead of previous solid state reaction for the system BaTiO3±Nb<sub...
[ 7 ] - Effect of Silicon Carbide and graphite additives on the pressureless Sintering mechanism and microstructural characteristics of Ultra-High Temperature ZrB2 Ceramics Composites
The effect of SiC content, additives, and process parameters on densification and microstructural properties of pressureless sintered ZrB2– (1–10 wt %) SiC particulate composites have been studied. The ZrB2–SiC composite powders mixed by Spex mixer with 1-2wt% C (added as graphite powder) and CMC have been cold-compacted and sintered in argon environment in the temperature range of 1800–2100ºC ...
[ 8 ] - Convectional hydrothermal synthesis of high-purity pesudo-cubic BaTi0.09Nb0.01O3 nanocrystals in rotary autoclave
Nano-sized BaTiO3 powders with particular Nb concentrations were prepared by Rotary- Hydrothermal (RH) method. Hydrothermal method was used at 180 °C for 5 hours with new Ti pressure and the teflon vessel was rotated at a speed of 160 rpm during the hydrothermal reaction. New hydrothermal method was used instead of previous solid state reaction for the system BaTiO3±Nb<sub...
[ 9 ] - Wear Behavior in Micro and Nano-Structured WC-9Co-0.7VC Cemented Carbide Produced by Rapid Hot Press Sintering
The effect of CaO on the formation of β- and γ-zirconia nanoparticles from α-zirconia was investigated and their stability evaluated via mechanical activation. α-ZrO2+8.5wt%CaO powder was milled for 2-150 hours with ball-to-powder weight ratios (BPWR) of 40:1 and 60:1. Structural evaluations were conducted using X-Ray diffraction and scanning electron microscope (SEM). Thermal analysis wa...
[ 10 ] - مشخصه یابی پوشش های نانوساختار سیستم Ti-Al-C-N ایجاد شده به روش رسوب دهی شیمیایی بخار به کمک پلاسما
در این تحقیق، پوشش های سرامیکی کربونیترید تیتانیوم آلومینیوم (TiAlCN) با مقادیر مختلفی از آلومینیوم در دمای °C 350 بر زیرلایه های فولاد ابزار گرم کار H13 با استفاده از روش رسوب شیمیایی بخار به کمک پلاسما (PACVD) نشانده شدند. مشخصه یابی پوشش های ایجاد شده با استفاده از آزمایش های پراش پرتو ایکس (GIXRD)، میکروسکوپ الکترونی روبشی گسیل میدانی (FESEM) و میکروسکوپ الکترونی روبشی(SEM) مجهز به آنالیزگر...