Tohid Saeid
Faculty of Materials Engineering, Sahand university of technology
[ 1 ] - Microstructural refining during friction stir processing of SAF 2205 duplex stainless steel
Friction stir processing (FSP) was conducted on a SAF 2205 duplex stainless steel at advancing speed of 50 mm/min and rotational speed of 400 rpm. Characterization of evolved material was studied using electron microscopy equipped with electron back scattered diffraction (EBSD) system. The results indicated that the severe plastic deformation and the heat generated during the FSP developed a v...
[ 2 ] - بررسی تاثیر شرایط عملیات حرارتی دو مرحله ای در ریزساختار و خواص مکانیکی فولادهای TRIP
فولادهای TRIP که یکی از انواع فولادهای استحکام بالای پیشرفته می باشند به دلیل دارا بودن ترکیب بسیار مناسبی از استحکام و شکلپذیری در دهههای اخیر مورد توجه پژهشگران قرار گرفتهاند. آستنیت باقیمانده در ریزساختار علت اصلی خواص مکانیکی مناسب این فولادهاست که با اعمال تغییر شکل مکانیکی به مارتنزیت تبدیل می شود و باعث بهبود خواص مکانیکی فولاد می گردد. ریزساختار خاص فولادهای TRIP از طریق یک عملیات حر...
[ 3 ] - بررسی تاثیر عملیات حرارتی فلز پایه بر ریزساختار آلیاژ برنج پس از فرایند اصطکاکی اغتشاشی
مس و آلیاژهای آن به علت داشتن ویژگی‌هایی از قبیل استحکام و داکتیلیته خوب، مقاومت به خوردگی بالا و هدایت الکتریکی و حرارتی بالا در مهندسی مواد بسیار کاربرد دارند. محدودیت جوشکاری مس و برنج‌ها در درجه اول ناشی ضریب بالای هدایت حرارتی آن‌ها و در درجه دوم از تبخیر فلز روی و در مرحله بعدی جذب هیدروژن و شکننده شدن درز جوش است. لذا برای غلبه بر این مشکلات فرایند اصطکاکی اغتشاشی به همراه عملیات حرارتی ...
[ 4 ] - جوشکاری همزن اصطکاکی فوم‌های آلومینیم تجاری خالص تولید شده به روش نورد تجمعی
در این تحقیق جوشکاری فوم�های آلومینیم خالص تجاری تولید شده به روش نورد تجمعی با استفاده از روش جوشکاری همزن اصطکاکی در سرعت�های چرخشی 500، 700، 900 و rpm1100 و سرعت خطی mm/min 25 بررسی شده است. تمامی جوش�ها به صورت بدون درز انجام شده است. برای بررسی درشت ساختار و سختی جوش�های انجام شده، متالوگرافی نوری و آزمون ریزسختی و به منظور تعیین درصد تخلخل فوم آلومینیمی و بررسی تغییرات چگالی ناحیه�ی جوش د...
[ 5 ] - Influence of rotational speed on the development of microstructure in a friction stir welded 304 austenitic stainless steel
Friction stir welding was conducted on AISI 304 austenitic stainless steel sheet with dimensions of 100 mm × 100 mm × 2 mm. The FSW was performed at a welding speed of 150 mm/min and rotational speeds of 400 and 800 rpm. The results showed that high frequency of low angle grain boundaries (LAGBs) were formed through dynamic recovery in the thermo-mechanically affected zone (TMAZ). Higher amoun...
[ 6 ] - Study of Microstracture and Microhardness of Welded Austenic Stainless Steel 316L by TIG, A-TIG and FB-TIG Methods.
In this study the effect of activating fluxes on the penetration depth, microstructure and microhardness of AISI316L austenitic stainless steel were evaluated by three TIG process variations (TIG, A-TIG and FB-TIG) and the results were compared together.. After selecting the optimal flux in the second stage, the effect of that on the penetration depth, microstructure and weld microhardness of ...
[ 7 ] - Microstructural evolution of 304 austenitic stainless steel in friction stir welding process
Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...
[ 8 ] - Influence of rotational speed on the development of microstructure in a friction stir welded 304 austenitic stainless steel
Friction stir welding was conducted on AISI 304 austenitic stainless steel sheet with dimensions of 100 mm × 100 mm × 2 mm. The FSW was performed at a welding speed of 150 mm/min and rotational speeds of 400 and 800 rpm. The results showed that high frequency of low angle grain boundaries (LAGBs) were formed through dynamic recovery in the thermo-mechanically affected zone (TMAZ). Higher amoun...
[ 9 ] - Study of Microstracture and Microhardness of Welded Austenic Stainless Steel 316L by TIG, A-TIG and FB-TIG Methods.
In this study the effect of activating fluxes on the penetration depth, microstructure and microhardness of AISI316L austenitic stainless steel were evaluated by three TIG process variations (TIG, A-TIG and FB-TIG) and the results were compared together.. After selecting the optimal flux in the second stage, the effect of that on the penetration depth, microstructure and weld microhardness of ...
[ 10 ] - Microstructural evolution of 304 austenitic stainless steel in friction stir welding process
Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...