A. R. Khorshidi
Department of Chemistry, Faculty of Sciences, University of Guilan, P.O.Box 41335-1914, Rasht, Iran
[ 1 ] - -OSO3H Functionalized Mesoporous MCM-41 Coated on Fe3O4 Nanoparticles: an Efficient and Recyclable Nano-Catalyst for Preparation of 3,2′-Bisindoles
Mesoporous MCM-41 was coated on Fe3O4 nanoparticles and then functionalized with sulfurochloridic acid to provide a core-shell solid acid nano-catalyst. The catalyst was characterized by transmission electron microscopy (TEM), infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TG), Brunauer-Emmet-Teller analysis (BET) and vibrating sample magnetometery (VSM). The...
[ 2 ] - Efficient Fenton like degradation of Methylene blue in aqueous solution by using Fe3O4 nanoparticles as catalyst
Fe3O4 nanoparticles were prepared hydrothermally and characterized by X-Ray diffraction spectroscopy (XRD), and scanning electron microscopy (SEM). It was found that these nanoparticles can act as an efficient catalyst in the degradation of Methylene blue dye in aqueous solution in a Fenton like system in presence of 30% perhydrol. Uv-Vis spectroscopy was used to determine the concentration of ...
[ 3 ] - Fe3O4@silica sulfuric acid nanoparticles as a potent and recyclable solid acid catalyst for the synthesis of indole derivatives
Fe3O4 magnetic nanoparticles were synthesized by co-precipitation of Fe2+ and Fe3+ in aqueous NaOH. Then silica was coated on the obtained nanoparticles and the whole composite was functionalized with chlorosulfonic acid in CH2Cl2. The obtained nanocomposite (Fe3O4@SiO2-SO3H) was characterized by FT-IR, VSM and XRD techniques and was used as an efficient catalyst in condensation reaction of ind...
[ 4 ] - تخریب رودامین 6G درمحلول آبی با استفاده از نانو ذرات هسته/پوسته Au/Fe3O4
در پژوهش حاضر نانوذرات مغناطیسی Fe3O4 به روش همرسوبی سنتز شدند و سپس پوسته طلا به روش احیای شیمیایی کلروآوریک اسید توسط سدیم بوروهیدرید تحت تابش فراصوت بر روی آنها روکش شد. نانوذرات Au/Fe3O4 بدست آمده با روشهای پراش سنجی پرتو ایکس و طیف سنجی تبدیل فوریه مادون قرمز مشخصه یابی شدند و ویژگیهای فیزیکی آنها توسط میکروسکوپ الکترونی روبشی و میکروسکوپ الکترونی عبوری بررسی شد. نانوذرات حاصل بعنوان کاتال...