[ 1 ] - The Influence of HH Type Steel Microstructure on the Distortion Behavior of Grate Bar Part in the Indurating Machine of Pelletizing Plant
Grate bar is an industrial part which is used in the indurating furnace of an iron ore pelletizing plant. Steel part ofthe grate bars are expected to have high resistance to atmospheric oxidation because of its contact with hot gases(up to 920 °C) during the normal operation of the process. In this study, different samples from several sections ofused grate bars with apparent ...
[ 2 ] - Synthesis and characterization of nHA-PLA composite coating on stainless steel by dip-coating process for biomedical applications
316L stainless steel is the most commonly used metallic material in the manufacture of orthopedic implants. To achive better properties metal implants often coated with biocomposites. A sol–gel method was used for coating of Poly lactic acid (PLA)/Hydroxyapatite nanopowder (nHA) on stainless steel 316L substrate. The X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) wer...
[ 3 ] - ایجاد شرایط بهینه جهت تولید گندله خام مناسب از کنسانتره‌های سنگ آهن با سطح ویژه پایین توسط افزودنی‌های آلی و معدنی
اساساً یکی از چالش‌های افزایش ظرفیت واحدهای گندله‌سازی در راستای برنامه افزایش تولید فولاد کشور، محدودیت در ظرفیت خردایش آسیاهای معادن سنگ آهن است. در سالهای اخیر دستیابی به اهداف تعیینشده منجر به کاهش سطح ویژه ذرات در طی فرآیند خردایش شده است. از این رو، هدف از این تحقیق ارائه راهکارهای اجرایی جهت دستیابی به تولید گندله خام مناسب از کنسانتره‌های سنگ آهن با سطح ویژه پایین (کمتر از cm2/g 1500...