[ 1 ] - Effects of Martensite Reversion Parameters on the Formation of Nano/ultrafine Grain Structure in AISI 304L Stainless Steel

Formation of nano/ultrafine grain structure in AISI 304L austenitic stainless steel through the martensite reversion treatment was studied. The solution annealed specimens were cold rolled up to 95 % thickness reduction at -15°C. The cold-rolled specimens were subjected to reversion annealing treatment at the temperature range of 700-1000 °C for 10–150 min. Microstructural evolutions were analy...