The Electrochemical Behavior of AISI 321 Stainless Steel in Alkaline Media
Authors
Abstract:
In this paper, the electrochemical behaviour of passive films formed on AISI 321 stainless steel (AISI 321) immersed in 0.1 M NaOH + 0.1 M KOH solution was evaluated by different electrochemical techniques. For this purpose, passive films were formed at open circuit potential for 1 to 12 hours and then electrochemical measurements were done. The polarization curves suggested that AISI 321 showed excellent passive behaviour in 0.1 M NaOH + 0.1 M KOH solution. Mott–Schottky analysis indicated that the accepted densities were in the range of 1021 cm-3 and decreased with immersion time. Electrochemical impedance spectroscopy (EIS) results showed that the best electrical equivalent circuit presented two time constants: The high-medium frequencies time constant could be correlated with the charge transfer process and the low frequencies time constant was associated with redox processes taking place in the surface film. Also, EIS results showed that polarization resistance was increased with formation time from 1 until 12 hours, due to the thickening of passive film.
similar resources
the electrochemical behavior of aisi 321 stainless steel in alkaline media
in this paper, the electrochemical behaviour of passive films formed on aisi 321 stainless steel (aisi 321)immersed in 0.1 m naoh + 0.1 m koh solution was evaluated by different electrochemical techniques. forthis purpose, passive films were formed at open circuit potential for 1 to 12 hours and then electrochemicalmeasurements were done. the polarization curves suggested that aisi 321 showed e...
full textThe Effect of Solution Concentration on the Electrochemical Behaviour of AISI 321 Stainless Steel in Sulfuric Solutions
full text
EFFECT OF IMMERSION TIME ON THE ELECTROCHEMICAL BEHAVIOUR OF AISI 321 STAINLESS STEEL IN 0.1 M H2SO4 SOLUTION
In this study, effect of immersion time on the electrochemical behaviour of AISI 321 stainless steel (AISI 321) in 0.1 M H 2SO 4 solution under open circuit potential (OCP) conditions was evaluated by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS). Mott–Schottky analysis revealed that the passive films behave as n-type and p-type s...
full textthe effect of solution concentration on the electrochemical behaviour of aisi 321 stainless steel in sulfuric solutions
full text
Effect of bonding temperature on the microstructure and electrochemical corrosion behavior of TLP bonded AISI 304L stainless steel
Transient liquid phase (TLP) bonding of AISI 304L stainless steel was carried out using BNi-2 amorphous interlayer. The microstructure of the joint area was studied by using optical and scanning electron microscopes and energy dispersive spectroscopy. The effect of bonding temperature (1030-1110 °C) was studied on the microstructure and corrosion behavior of the TLP bonded samples. Electrochemi...
full textEffect of bonding temperature on the microstructure and electrochemical corrosion behavior of TLP bonded AISI 304L stainless steel
Transient liquid phase (TLP) bonding of AISI 304L stainless steel was carried out using BNi-2 amorphous interlayer. The microstructure of the joint area was studied by using optical and scanning electron microscopes and energy dispersive spectroscopy. The effect of bonding temperature (1030-1110 °C) was studied on the microstructure and corrosion behavior of the TLP bonded samples. Electrochemi...
full textMy Resources
Journal title
volume 10 issue 1
pages 7- 13
publication date 2013-07-01
By following a journal you will be notified via email when a new issue of this journal is published.
Keywords
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023