The Effect of Heat Treatment on the Microstructure and Mechanical Properties of Al/Al3Zr + Al3Ti In-situ Hybrid Composite Fabricated by Friction Stir Processing

Authors

  • Ranjbar, Khalil Department of Materials Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran.
Abstract:

In this research, an in-situ hybrid composite reinforced by Al3Zr and Al3Ti aluminide particles was fabricated by friction stir processing (FSP). The base metal was in the form of a rolled Al 3003-H14 alloy sheet, and zirconium and titanium metal powders were used as the reinforcements. Six passes of FSP were applied. Tensile strength and hardness of the base metal, as well as FSPed samples before and after applying heat treatment, were determined. Microstructural examinations were performed using optical and scanning electron microcopy (SEM), and phase formation was identified by X-Ray diffraction. Microstructural examination revealed that by applying FSP, the prior large and elongated grains of the base metal were converted to the fine and equiaxed grains. It was also observed that chemical reactions occurred at the interface between the aluminum matrix and the metallic powders, forming in-situ aluminides of Al3Zr and Al3Ti. The post annealing heat treatment activated these solid state chemical reactions and more aluminides were formed. It was also found that the heat treated hybrid composite possessed the highest tensile strength and hardness values. The tensile strength in such samples reached 195 MPa, as compared to 110 MPa of the base metal.

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

Effect of Heat Input on Microstructure and Mechanical Properties in Friction Stir Welding of HSLA-60

High-strength low alloy steels are a class of steels used in applications that require high strength and good weldability, including ship hulls, gas pipelines and oil industry. One way to build parts is fusion welding that create areas with a large grain size in the heat-affected zone and increased susceptibility to hydrogen cracking. One way to solve this problem is to use solid state friction...

full text

Effect of Heat Input on Microstructure and Mechanical Properties in Friction Stir Welding of HSLA-60

High-strength low alloy steels are a class of steels used in applications that require high strength and good weldability, including ship hulls, gas pipelines and oil industry. One way to build parts is fusion welding that create areas with a large grain size in the heat-affected zone and increased susceptibility to hydrogen cracking. One way to solve this problem is to use solid state friction...

full text

The Effect of Friction Stir Processing Speed Ratio on the Microstructure and Mechanical Properties of A 430 Ferritic Stainless Steel

This study is an attempt to investigate the effect of welding rotational and traverse speed on mechanical and microstructural properties of A 430 stainless steel in order to give an effective processing window to achieve an appropriate microstructure and so mechanical properties. There are a wide range industrial uses for ferritic stainless steel. There from they have some problems like grain c...

full text

the effect of taftan pozzolan on the compressive strength of concrete in the environmental conditions of oman sea (chabahar port)

cement is an essential ingredient in the concrete buildings. for production of cement considerable amount of fossil fuel and electrical energy is consumed. on the other hand for generating one tone of portland cement, nearly one ton of carbon dioxide is released. it shows that 7 percent of the total released carbon dioxide in the world relates to the cement industry. considering ecological issu...

the washback effect of discretepoint vs. integrative tests on the retention of content in knowledge tests

در این پایان نامه تاثیر دو نوع تست جزیی نگر و کلی نگر بر به یادسپاری محتوا ارزیابی شده که نتایج نشان دهندهکارایی تستهای کلی نگر بیشتر از سایر آزمونها است

15 صفحه اول

Effect of heat treatment on the grain structure and mechanical properties of Al-7075 friction stir weld

The fine grain structure of friction-stir welded aluminum alloys is unstable during post weld heat treatment and some grains abnormally grown. In this study, the sequence of abnormal grain growth during T6 heat treatment of Al-7075 friction-stir weld and its effect on mechanical properties of the weld was studied. The results showed that heat treatment in 510 ˚C resulted in drastic grain growth...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 38  issue 1

pages  49- 64

publication date 2019-06

By following a journal you will be notified via email when a new issue of this journal is published.

Keywords

No Keywords

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023