Synthesis, Characterization and Vapor Permeation Performance of B-ZSM-5 Membranes
Authors
Abstract:
In the present work, B-ZSM-5 zeolite membranes were synthesized on porous tubular α-alumina supports by several subsequence in situ crystallization hydrothermal treatments. The TiO2- Bohmite and ɣ- alumina intermediate layers were applied to improve the lattice matching between zeolite layer and the support. The uniform membrane intermediate layers with low permeation resistance were prepared on the alumina support surface. The N2 permeance of the intermediate layers and support showed that after the modification of the support surface with ɣ-alumina the Knudsen diffusion can be the dominant mechanism. Selectivity of binary mixture of normal pentane (n-C5) and iso-pentane (i-C5) through B-ZSM-5 zeolite membrane was investigated as a function of feed pressure, temperature and sweep gas flowrate in vapor permeation membrane process using the concentration gradient method. The selectivity results depend strongly on the measurement conditions. The obtained results showed that rising sweep gas flowrate from 5ml/min to 15 ml/min, feed pressure from 1.05 bar to 1.3 bar and decreasing temperature from 200°C to 150°C increased the driving force for n-C5 transfer across the membrane. The selectivity of n-C5/i-C5 8.2 was obtained at 150°C for sweep gas flow of 5 ml/min and 10.4 for sweep gas flow of 10ml/min.
similar resources
synthesis, characterization and vapor permeation performance of b-zsm-5 membranes
in the present work, b-zsm-5 zeolite membranes were synthesized on porous tubular α-alumina supports by several subsequence in situ crystallization hydrothermal treatments. the tio2- bohmite and ɣ- alumina intermediate layers were applied to improve the lattice matching between zeolite layer and the support. the uniform membrane intermediate layers with low permeation resistance were prepared o...
full textsynthesis and characterization of some macrocyclic schiff bases
ماکروسیکلهای شیف باز از اهمیت زیادی در شیمی آلی و دارویی برخوردار می باشند. این ماکروسیکلها با دارابودن گروه های مناسب در مکانهای مناسب می توانند فلزاتی مثل مس، نیکل و ... را در حفره های خود به دام انداخته، کمپلکسهای پایدار تولید نمایند. در این پایان نامه ابتدا یک دی آلدئید آروماتیک از گلیسیرین تهیه می شود و در مرحله بعدی واکنش با دی آمینهای آروماتیک و یا آلیفاتیک در رقتهای بسیار زیاد منجر به ت...
15 صفحه اولCatalytic Performance and Characterization of Promoted K-La/ZSM-5 Nanocatalyst for Biodiesel Production
The promoted K-La nanocatalysts supported on ZSM-5 zeolite were prepared via wetness impregnation method and tested for biodiesel production from soybean oil. The effects of different weight percentage of La, loading of K as a promoter and calcination conditions on structure and activity of catalyst were investigated. Results showed that the supported catalyst containing 7wt.% of La was pro...
full textCharacterization of Commercial Ceramic and Hybrid Membranes Using Gas Permeation and Permporometry Tests
The gas separation performance of commercial ceramic Titania and hybrid silica (HybSi®) membranes was assessed using the gas permeation and permporometry methods. Results indicated that the HybSi® membranes have a hybrid surface containing regions covered by a polymeric matrix and others with inorganic pores. These membranes have high H2 selectivity, which incre...
full textsynthesis and characterization of potentially biological active cyclometallated organoplatinum(ii) complexes
this work is presented in five parts. in the first part preparation of the starting complex [pt(c^n)cl(dmso)], 1, in which c^n = n(1),c(2?)-chelated, deprotonated 2-phenylpyridine, and dmso = dimethylsulfoxide, and its reaction with 1 equiv of the biphosphine ligands bis(diphenylphosphino)amine, dppa, or bis(diphenylphosphino)methane, dppm, to give the complex [pt(c^n)cl(dppa)], 2, or [pt(c^n)c...
15 صفحه اولsynthesis and characterization of some new cyclometalated organoplatinum(ii) complexes containing phosphite ligand
در این تحقیق روشی جهت سنتز یک سری از کمپلکس های پلاتین (ii) حاوی لیگاند های دهنده ی فسفری شامل فسفیت و فسفین ارائه شده است. واکنش پیش ماده ی پلاتین (ii)،trans/cis- [ptcl2(sme2)2] ، با 2 اکی مولار از لیگاند p(oph)3در حلال بنزن کمپلکس1، cis-[ptcl2(p(oph)3)2] را تولید می نماید. جهت سنتز کمپلکس سایکلو متال فسفیتی، کمپلکس 1 با 1 اکی والان واکنشگر ptcl2 در حلال زایلن در شرایط رفلاکس زیر گاز آرگون م...
My Resources
Journal title
volume 3 issue Number 1
pages 31- 42
publication date 2016-12-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023