Synthesis and Characterization of PbTiO3 Nanopowders by Citric Acid Gel Method
Authors
Abstract:
High purity lead titanate nanopowders in tetragonal form have been successfully prepared bycitric acid gel method using lead nitrate and tetra-n-butyl titanate as Pb and Ti sourcesrespectively and citric acid as complexing reagent. The precursors were calcined at varioustemperatures ranging from 450 °C to 600 °C for 2 h. Fourier Transform InfraredSpectroscopy (FT-IR), X-ray diffraction (XRD) and Transmission Electron Microscopy(TEM) were used to characterize the crystallization process, particle size and morphology ofthe calcined powders. The results indicated that lead titanate nanoparticles with an averagesize ranging from 35-50 nm could be obtained after calcining of the dried gel at 550°C for2 h.
similar resources
synthesis and characterization of pbtio3 nanopowders by citric acid gel method
high purity lead titanate nanopowders in tetragonal form have been successfully prepared bycitric acid gel method using lead nitrate and tetra-n-butyl titanate as pb and ti sourcesrespectively and citric acid as complexing reagent. the precursors were calcined at varioustemperatures ranging from 450 °c to 600 °c for 2 h. fourier transform infraredspectroscopy (ft-ir), x-ray diffraction (xrd) an...
full textSynthesis, characterization, of Fluorohydroxyapatite nanopowders by sol-gel processing
In this work, sol-gel processing was used to synthesize the fluorohydroxyapatite (nano-FHA, Ca10(PO4)6(OH)2−xFx) nanopowders. The advantages of the sol-gel method over other methods are precise control of composition, low processing temperature, and better homogeneity. Calcium nitrate tetrahydrate, phosphorous pentoxide and Tetrabuthylammon...
full textSynthesis, characterization, of Fluorohydroxyapatite nanopowders by sol-gel processing
In this work, sol-gel processing was used to synthesize the fluorohydroxyapatite (nano-FHA, Ca10(PO4)6(OH)2−xFx) nanopowders. The advantages of the sol-gel method over other methods are precise control of composition, low processing temperature, and better homogeneity. Calcium nitrate tetrahydrate, phosphorous pentoxide and Tetrabuthylammon...
full textStructural characterization of BaZrO3 nanopowders prepared by stearic acid gel method
Pure barium zirconate nanopowders were successfully prepared in wet-chemistry synthesismethod, using barium stearate and tetra-n-butyl zirconate as Ba, Zr sources and stearic acid ascomplexing reagent. The gel was calcined at 800 and 900 °C in air. Results of thermal analysisare given, including both DTG and TG. Fourier transform infrared spectrometry (FTIR), X-raydiffraction (XRD), transmissio...
full textStructural characterization of Ba1.„Sr„TiO3 (BST) nanopowders prepared by stearic acid gel method
Stoichiometric tetragonal Bal-xSrxTiO3 (x = 0.23) nanopowders were prepared by stearic acid gel(SAG) method using barium stearate, strontium stearate, tetrabutyl titanate as Ba, Sr, Ti sourcesand stearic acid as complexing reagent. Thermal analysis including differential thermogravimetric(DTG) and TG, Fourier transform infrared spectrometry (FTIR), X-ray diffraction (XRD) andtransmission electr...
full textsynthesis, characterization, of fluorohydroxyapatite nanopowders by sol-gel processing
in this work, sol-gel processing was used to synthesize the fluorohydroxyapatite (nano-fha, ca10(po4)6(oh)2−xfx) nanopowders. the advantages of the sol-gel method over other methods are precise control of composition, low processing temperature, and better homogeneity. calcium nitrate tetrahydrate, phosphorous pentoxide and tetrabuthylammonium fluoride were used, respectively, as p, ca, and f p...
full textMy Resources
Journal title
volume 6 issue 1
pages 9- 12
publication date 2009-05-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023