Studying the Effect of the Concentration of PTFE Nanoparticles on the Tribological Behavior of Ni-P-PTFE Composite Coatings

In the past 30 years, electroless nickel (EN) plating has grown to such proportions that these coatings and their applications are now found underground, in outer space, and in a myriad of areas in between. Moreover, in order to further improve the mechanical and tribological properties of the nickel-phosphorous (Ni-P) coatings, Ni-P/PTFE composite coatings can be obtained, which provides even greater friction behavior and lubricity than the one naturally occurring in the nickel-phosphorous alloy deposit. In this paper, The Ni-P-PTFE coating was deposited on mild carbon steel surface via electroless deposition process. The friction behavior and wear mechanisms of Ni-P-PTFE nanocomposite coating were studied at different concentrations of PTFE. Frictional behavior was examined using a pin on disk wear test method. Surface morphology and worn surface was evaluated using field emission scanning electron microscopy (FESEM) and energy dispersive spectroscopy (EDS) analysis. The results showed that the incorporation of PTFE nanoparticles can reduce the wear rate of Ni-P coating from 33.07×10-6 mm3/Nm to 12.46×10-6 mm3/Nm for the Ni-P PTFE containing 10 g/l PTFE and decrease the friction coefficient from 0.64 to 0.2. Thus the tribological behavior of Ni-P coating is much improved in the presence of PTFE nanoparticles and 10 g/l is the optimized concentration of PTFE in the electroless bath.