Photo catalytic property of ZnO and Mn-ZnO nanoparticles in removal of Cibacet Turquoise blue G from aquatic solution
Authors
Abstract:
ZnO and Mn-ZnO nano powders were prepared by the sol-gel auto combustion method. The products were characterized by X-ray diffraction (XRD), energy dispersive analysis of X-ray (EDX) and scanning electron microscopy (SEM). Structural and morphological properties of nano particles were investigated and the average crystalline size of ZnO and Mn-doped ZnO was obtained 44 and 51 nm, respectively. Also, photo catalytic removal of Cibacen Turquoise Blue G dye from aqueous solution by using nano scale ZnO and Mn-ZnO powders under UV light irradiation was studied. The effect of initial dye concentrations and dosage of photo catalysts, were investigated in the photo destructive process. This is 57% of dye degraded by 0.02 mg of ZnO in 70 minutes. The degradation rate increase to 84% in the presence of 0.02 mg of Mn-ZnO in the same time.
similar resources
photo catalytic property of zno and mn-zno nanoparticles in removal of cibacet turquoise blue g from aquatic solution
zno and mn-zno nano powders were prepared by the sol-gel auto combustion method. the products were characterized by x-ray diffraction (xrd), energy dispersive analysis of x-ray (edx) and scanning electron microscopy (sem). structural and morphological properties of nano particles were investigated and the average crystalline size of zno and mn-doped zno was obtained 44 and 51 nm, respectively. ...
full textSol-gel Synthesis of ZnO Nanoparticles and ZnO-TiO2-SiO2 Nanocomposites and Their Photo-catalyst Investigation in Methylene Blue Degradation
In this work firstly ZnO nanoparticles were synthesized via a simple precipitation method. At the second step titanium dioxide and silicon dioxide shell were synthesized on the core. For preparation ZnO-TiO2-SiO2 the sol product was calcinated at 500 ºC for 2h. Properties of the product were examined by X-raydiffraction pattern (XRD), scanning electron microscope (SEM) and Fourier transform inf...
full textFerromagnetic ordering in Mn-doped ZnO nanoparticles
Zn1 - x Mn x O nanoparticles have been synthesized by hydrothermal technique. The doping concentration of Mn can reach up to 9 at% without precipitation or secondary phase, confirmed by electron spin resonance (ESR) and synchrotron X-ray diffraction (XRD). Room-temperature ferromagnetism is observed in the as-prepared nanoparticles. However, the room-temperature ferromagnetism disappears after ...
full textRemoval of Lead from Aquatic Solution Using Synthesized Iron Nanoparticles
Due to its ability in chemical oxidation of contaminants, iron nanoparticle is a material of choice to remove lead ions from aquatic solutions. In this study a reduction method in solution phase was applied to synthesize thenanoparticles. Afterwards, the size of the synthesized particles were confirmed by Scanning Electron Microscopy. It is worth noting that th...
full textsol-gel synthesis of zno nanoparticles and zno-tio2-sio2 nanocomposites and their photo-catalyst investigation in methylene blue degradation
in this work firstly zno nanoparticles were synthesized via a simple precipitation method. at the second step titanium dioxide and silicon dioxide shell were synthesized on the core. for preparation zno-tio2-sio2 the sol product was calcinated at 500 ºc for 2h. properties of the product were examined by x-raydiffraction pattern (xrd), scanning electron microscope (sem) and fourier transform inf...
full textMy Resources
Journal title
volume 5 issue 2
pages 145- 154
publication date 2014-04-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023