Microstructural Evolution of X45CrNiW189 Valve Steel During Hot Deformation
Authors
Abstract:
The hot compression tests were carried on X45CrNiW189 valve steel (X45) in the temperature range of 1000– 1200 °C and the strain rate range of 0.004 – 0.5 s-1 in order to study the high temperature softening behavior of this steel. For the exact prediction of flow stress, the effective stress-effective strain curves were obtained from experiments under various conditions. On the basis of experimental results, the dynamic recrystallization fraction (DRX), austenite grain size (AGS), hot deformation and activation energy behavior were investigated. It was found that the calculated results were in a good agreement with the experimental flow stress and the microstructure of the steel for different conditions of hot deformation.
similar resources
microstructural evolution of x45crniw189 valve steel during hot deformation
the hot compression tests were carried on x45crniw189 valve steel (x45) in the temperature rangeof 1000– 1200 °c and the strain rate range of 0.004 – 0.5 s-1 in order to study the high temperaturesoftening behavior of this steel. for the exact prediction of flow stress, the effective stress-effectivestrain curves were obtained from experiments under various conditions. on the basis of experimen...
full textMicrostructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation
Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to dif...
full textMicrostructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation
Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to dif...
full textThe Strain Dependence of Post-Deformation Softening during the Hot Deformation of 304H Stainless Steel
Experiments were carried out in which the dependence of the fractional softening on temperature, time and strain rate was determined in a 304H stainless steel. Three prestrain ranges were identified pertaining to three different post-deformation softening behaviors: 1) prestraining to below the DRX critical strain: strongly strain dependent softening by SRX alone with softening kinetics control...
full textMicrostructural Evolution and Dynamic Softening Mechanisms of Al-Zn-Mg-Cu Alloy during Hot Compressive Deformation
The hot deformation behavior and microstructural evolution of an Al-Zn-Mg-Cu (7150) alloy was studied during hot compression at various temperatures (300 to 450 °C) and strain rates (0.001 to 10 s-1). A decline ratio map of flow stresses was proposed and divided into five deformation domains, in which the flow stress behavior was correlated with different microstructures and dynamic softening m...
full textMicrostructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
full textMy Resources
Journal title
volume 11 issue 1
pages 31- 34
publication date 2015-03-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023