MECHANO-THERMAL REDUCTION OF HEMATITE AND ANATASE MIXTURE BY TWO DIFFERENT FORMS OF CARBON AS REDUCTANT FOR IN-SITU PRODUCTION OF Fe-T iC - NANO CRYSTALLINE COMPOSITE
Authors
Abstract:
In this research, two different carbonaceous materials (Graphite:G and Petrocoke:P) were separately compared in terms of the carbothermic reduction of hematite and anatase in order to synthesize Fe-TiC nanocrystalline composite by mechanically activated sintering method. Powders were activated in a planetary high-energy ball mill under argon atmosphere for 0, 2, 5, 10,and 20 h. Then, the activated powders were analyzed by XRD and SEM to investigate phase constituents and microstructure of the mixtures. Results proved that Fe 2 O 3 and TiO 2 were not reduced by carbonaceous materials even after 20h of milling. SEM investigations showed that G-mixture was more homogenous than P-mixture after 20h of milling, meaning that graphite-anatase-hematite was mixed satisfactorily. Thermogravimetry analysis was done on 0 and 20h milled powders. TG and DTG curves showed that mechanical activation led to almost 300°C decrease in the reduction temperature of hematite and anatase in both mixtures. In the next step, the powders were sintered in a tube furnace under argon atmosphere. In the G-mixture, anatase was reduced to titanium carbide at 1100°C but, in the P-mixture, temperature of 1200°C was essential for completely reducing anatase to titanium carbide.Results of phase identification of the sintered powders showed that anano-crystalline ironbased composite with titanium carbide, as the reinforcement was successfully synthesized after 20 h high-energy milling of the initial powders and subsequent sintering occurred at 1200˚C for 1h
similar resources
suppression of coke formation in thermal cracking by coke inhibitors
the main purpose of this research was to:1.develop a coking model for thermal cracking of naphtha.2.study coke inhibition methods using different coke inhibitors.developing a coking model in naphtha cracking reactors requires a suitable model of the thermal cracking reactor based on a reliable kinetic model.to obtain reliable results all these models shall be solved simultaneously.for this pu...
15 صفحه اولstudy of cohesive devices in the textbook of english for the students of apsychology by rastegarpour
this study investigates the cohesive devices used in the textbook of english for the students of psychology. the research questions and hypotheses in the present study are based on what frequency and distribution of grammatical and lexical cohesive devices are. then, to answer the questions all grammatical and lexical cohesive devices in reading comprehension passages from 6 units of 21units th...
nano-rods zno as an efficient catalyst for the synthesis of chromene phosphonates, direct amidation and formylation of amines
چکیده ندارد.
application and construction of carbon paste modified electrodes developed for determination of metal ions in some real samples
ساخت الکترودهاِی اصلاح شده ِیکِی از چالشهاِی همِیشگِی در دانش شیمِی بوِیژه شیمِی تجزیه مِی باشد ،که با در نظر گرفتن سادگِی ساخت، کاربردی بودن و ارزان بودن روش مِی توان به باارزش بودن چنِین سنسورهاِی پِی برد.آنچه که در ادامه آورده شده به ساخت و کاربرد الکترودهاِی اصلاح شده با استفاده از نانو ذرات در اندازه گِیرِی ولتامترِی آهن وکادمِیم اشاره دارد. کار اول اختصاص دارد به ساخت الکترود خمِیر کربن اصلاح شده با لِیگاند داِ...
15 صفحه اولcomparison of the amount of debris extruded apically in two rotary techniques: flexmaster and m2
چکیده ندارد.
15 صفحه اولsynthesis of 3-aryl-2h-benzo[b]-1,4-oxazines in [omim]bf4 and reduction of organic compounds in methylimidazolium formate
در این پروژه ترکیبات 3-آریل-2h-بنزو[b]-4،1-اکسازین ها از مواد اولیه تجاری مشتقات دو آمینو فنول و ?-هالو کتون های آروماتیک در مایع یونی 1-اکتیل-3-متیل ایمیدازولیوم تترا فلورو بورات([omim]bf4) سنتز شده است. این واکنش توسط باز پتاسیم کربنات محلول از طریق o-آلکیلاسیون و سپس یک واکنش آمیداسیون درون مولکولی خود بخود در مدت زمان کوتاه انجام می شود. ترکیبات 4،1-بنزوکسازین به این روش با بهره خوب تا آلی ...
15 صفحه اولMy Resources
Journal title
volume 12 issue 2
pages 56- 70
publication date 2015-06
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023