Kinetics of chemical leaching of chalcocite from low-grade copper ore: size-distribution behavior
Authors
Abstract:
Kinetics of the chemical leaching of chalcocite from a low-grade copper ore in a ferric sulfate medium was investigated using the constrained least square optimization technique. The experiments were carried out for different particle sizes in both the reactor and column at constant Eh, pH, and temperature. The leaching rate increased with increase in the temperature. About 50% of the Cu recovery was obtained after 2 hours of reactor leaching at 75 o C using the -0.5 mm size fraction. Also about 50% of the Cu recovery was obtained after 60 days of column leaching for the +4-8 mm size fraction. For the fine-particle leaching, the first leaching step was fast, and the rate controlling step was diffusion through the liquid film. The results obtained show that as the leaching proceeds, the chemical reaction control appears. Finally, accumulation of the elemental sulfur layer in the solid product together with the jarosite precipitate causes change in the controlling mechanism to solid diffusion. For the coarse-particle leaching, diffusion through the solid product appeared from the initial days of leaching.
similar resources
kinetics of chemical leaching of chalcocite from low-grade copper ore: size-distribution behavior
kinetics of the chemical leaching of chalcocite from a low-grade copper ore in a ferric sulfate medium was investigated using the constrained least square optimization technique. the experiments were carried out for different particle sizes in both the reactor and column at constant eh, ph, and temperature. the leaching rate increased with increase in the temperature. about 50% of the cu recove...
full textInvestigation of leaching kinetics of zinc from a low-grade ore in organic and inorganic acids
The leaching kinetics of a low-grade zinc oxide ore in different acid media was investigated with respect to the experimental variables including acid concentration, temperature, liquid to solid (L/S) ratio, and stirring speed. The results obtained showed that the leaching reagent concentration and the reaction temperature exerted significant effects on the extraction of zinc, whereas the L/S r...
full textInvestigation of Leaching Kinetics of Smithsonite Ore
The leaching kinetics of smithsonite ore in acetic acid solutions, an environmental friend, and natural reagent was investigated. The influence of parameters such as reaction temperature, particle size, solid-liquid ratio and acid concentration was studied in order to reveal the leaching kinetics of smithsonite ore. In this study, experimental and statistical methods were carried out in order t...
full textLeaching of Lead and Zinc from a Low-Grade Oxide Ore in Citric Acid Media
Leaching of a low-grade lead and zinc oxide ore was studied by an organic reagent, citric acid. The quadratic mathematical models were developed for the relationship among the influential parameters and lead and zinc recoveries. Leaching rate was strongly affected by the interactive effects of factors. It was also found that the quadratic effects of stirring speed and linear<e...
full textOptimization of parameters affecting recovery of copper from Sarcheshmeh low-grade sulfide ore using Bioleaching
In this work, the parameters affecting the recovery of copper from the low-grade sulfide minerals of Sarcheshmeh Copper Mine were studied. A low-grade sulfide ore was used with a copper grade of 0.25%, which was about 28% of the mineral oxide, and the sulfide minerals made up the rest. Much more sulfide minerals were found to be pyrite and most of the gangue minerals were quartz, anorthite, bio...
full textMy Resources
Journal title
volume 6 issue 1
pages 109- 118
publication date 2015-02-22
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023