Influence of Alumina nano particles addition on the properties of wall tiles containing slag

Authors

Abstract:

The use of waste materials and industrial wastes in order to protect the environment and also to reduce costs has been considered. In this study, first, the use of slag, a waste of the steel industry, on the properties of the wall tile body was investigated. For this purpose, different percentages of slag were added to the tile body and physical properties such as density, percentage of shrinkage after sintering, open porosity, bending strength and microstructure were investigated. According to the results, the use of slag leads to the formation of anorthite and wollastonite phases in the tile body. The results showed that slag up to 30 wt% leads to increased density, reduced shrinkage and improved bending strength of tiles. The bending strength of the tile body increased from 23.6 MPa to 33.8 MPa for a body containing 30 wt% slag. The strength improvement can be attributed to the lower porosity, the formation of needle-shaped anorthite and wollastonite phases by using slag. Then, the effect of alumina nanoparticles in the amounts of 1, 2 and 3 wt% on the properties of the tile body containing 30 wt% slag was investigated. The addition of nano-alumina particles increased the bending strength of the tile body and the bending strength for the body containing 3 wt% reached 39.5 MPa. The increase in strength can be related to the higher percentage of anorthite phase in the presence of nano-alumina.  

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

the influence of the neo-platonic concept of poetic imagination on wordsworth’s poetry

بر اساس نظریه افلاطون در باره شعر خلاقیت هنری مورد انتقاد قرار گرفته است. نظریه کلی در مورد شعر این بود که شعر از ظواهرتقلید میکند و نه حقیقت. چون سایه ای از حقیقت است. اما با پیدایش فلسفه نو افلاطونی، انتقاتات قبلی در مورد شعر و شاعری اصلاح شد. فلوطین در کتاب انئید، اساس خلق هنری را بر محور مُثل افلاطونی قرار داد. وی باور داشت که هنر مندان در خلق آثار هنری، تحت تاثیر مُثل افلاطونی بوده و عوالمی ...

control of the optical properties of nanoparticles by laser fields

در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...

15 صفحه اول

INFLUENCE OF NANO SILICA ON PROPERTIES AND MICROSTRUCTURE OF HIGH ALUMINA ULTRA-LOW CEMENT REFRACTORY CASTABLES

Colloidal silica bonded refractory castables have been developed recently. It was found that colloidal silica is one of the best binders can substitute other binders such as cement in No Cement Castable (NCC) and Ultra Low Cement Castable (ULCC) refractories. Also composition of colloidal silica with appropriate additives resulted in a gel form which makes the initial strength. Moreover, the na...

full text

synthesis of amido alkylnaphthols using nano-magnetic particles and surfactants

we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.

15 صفحه اول

Influence of Nano-Particles on Characteristics of MetakaolinContained Cement Paste

The influences of nano-ZrO2 (NZ), nano-TiO2 (NT), nano-Fe2O3 (NF) and nano-Al2O3 (NA) additions on properties of the fresh and hardened cement paste in comparison with the fine cement paste were experimentally studied. Mini slump and flow cone tests were conducted on fresh cement pastes. Moreover the compressive and tensile strength of hardened cement paste were measured. SEM micrographs and XR...

full text

the effect of taftan pozzolan on the compressive strength of concrete in the environmental conditions of oman sea (chabahar port)

cement is an essential ingredient in the concrete buildings. for production of cement considerable amount of fossil fuel and electrical energy is consumed. on the other hand for generating one tone of portland cement, nearly one ton of carbon dioxide is released. it shows that 7 percent of the total released carbon dioxide in the world relates to the cement industry. considering ecological issu...

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 18  issue 1

pages  48- 56

publication date 2022-05

By following a journal you will be notified via email when a new issue of this journal is published.

Keywords

No Keywords

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023