Grain Refinement and Enhancement of Mechanical Properties of Hot Extruded Rare-Earth Containing Magnesium Alloy
Authors
Abstract:
The effects of rare earth addition and hot extrusion process on the grain refinement of magnesium alloy were studied. The as-cast Mg-6Al-1Zn (AZ61) alloy had the average grain size of ~ 64 µm and its microstructure consisted of α-Mg and Mg17Al12 phase. By partial substitution of Al with Gd to reach Mg-4.8Gd-1.2Al-1Zn alloy, it was observed that the Mg17Al12 phase disappeared and two new intermetallic phases, i.e. (Mg,Al)3Gd and Al2Gd, were identified. The extrusion process showed significant effects on the shape and size of intermetallics and grain size of the matrix. The grain size of the extruded Mg-6Al-1Zn alloy was refined from 64 µm to 13.4 µm as a result of recrystallization. Regarding the Mg-4.8Gd-1.2Al-1Zn alloy, the grain refinement was much more pronounced, where the extruded grain size has been refined from 698 µm to 2.4 µm (extruded at 385 °C) and 1.3 µm (extruded at 320 °C). This was related to the presence of fine and widely dispersed intermetallic phases. Tensile strength and total elongation of extruded alloys were much higher than their as-cast counterparts and the extruded Mg-6Zn-1Al alloy showed magnificent mechanical properties. The latter was related to the absence of intermetallic particles, which act as stress risers.
similar resources
Mechanical Properties of Magnesium-Rare Earth Alloy Systems: A Review
Magnesium-rare earth based alloys are increasingly being investigated due to the formation of highly stable strengthening phases, activation of additional deformation modes and improvement in mechanical properties. Several investigations have been done to study the effect of rare earths when they are alloyed to pure magnesium and other Mg alloys. In this review, the mechanical properties of the...
full textdetermination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولthe effects of mechanical vibration, grain refinement and modification on the structure and mechanical properties of a380 aluminum alloy
this research concentrates on the effects of low frequency, vertical mechanical vibration during solidification on the microstructure and mechanical properties of a380 aluminum alloy. two series of sr-modified and al-5ti-b grain refined a380 alloy samples were solidified in both static and dynamic conditions in the frequency and amplitude of 60 hz and 0.2 m, respectively. their physical, micro-...
full textMagnificent Grain Refinement of Al-Mg2Si Composite by Hot Rolling
The effect of chemical composition and the hot rolling operations on the microstructure and mechanical properties of in situ aluminum matrix composite with Mg2Si phase as the reinforcement was studied. It was revealed that the modification by phosphorous results in the rounder (more spherical) primary and secondary (eutectic) magnesium silicide intermetallics. During hot rolling, the primary pa...
full textsome properties of fuzzy hilbert spaces and norm of operators
in this thesis, at first we investigate the bounded inverse theorem on fuzzy normed linear spaces and study the set of all compact operators on these spaces. then we introduce the notions of fuzzy boundedness and investigate a new norm operators and the relationship between continuity and boundedness. and, we show that the space of all fuzzy bounded operators is complete. finally, we define...
15 صفحه اولMy Resources
Journal title
volume 50 issue 2
pages 132- 136
publication date 2017-12-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023