Grafting of Maleic Anhydride onto Co)propylene-b-ethylene( by Extrusion Process: Measurement of Adhesion to Steel Surface
Authors
Abstract:
Polypropylene (PP) has poor adhesion to metals and other surfaces for its chemical structure. Hence, chemical modification of PP is necessary for metal surface coating application. In this research, grafting of maleic anhydride (MA) onto co(propylene-b-ethylene) in the presence of a dicumyl peroxide (DCP) was accomplished in a single screw extruder. Characteristics of the modified polymer were determined by Infra-red Spectroscopy (IR), Scanning Electron Microscopy (SEM), and adhesion test. Maximum grafting of MA was found to be 1.2832% for 1.5 pph of MA. Adhesion test showed that the samples containing 1 pph of MA (degree of grafting is 0.5816%) had better adhesion to steel surface (17.25 kgf).
similar resources
Grafting of Tetrahydrophthalic and Maleic Anhydride Onto Polyolefins in Solution
Polietileno de baixa densidade (LLDPE) com comonômeros 1-buteno e 1-octeno foram funcionalizados com anidrido tetrahidroftálico (THA) e anidrido maléico (MA) em solução na presença de peróxido de benzoíla (BPO), de acordo com planejamentos fatoriais. As variáveis testadas foram concentração de anidrido, concentração de peróxido, tempo de reação e tipo de comonômero. As formulações foram analisa...
full textComparison of grafting of maleic anhydride onto linear low density polyethylene with hexene-1 and butene-1 comonomers and prediction of optimum ingredients by response surface methodology
In this work, the grafting of maleic anhydride onto two types of linear low density polyethylene with hexene-1 comonomer (LLDPE-H1) and butene-1 comonomer (LLDPE-B1), in the presence of styrene monomer (St) and dicumyl peroxide initiator (DCP) has been studied. The combined influences of MAH, St and DCP on the grafting efficiency via a melt reactive mixing process have been investigated using r...
full textMelt Free-Radical Grafting of Maleic Anhydride onto Biodegradable Poly(lactic acid) by Using Styrene as a Comonomer
Maleic anhydride (MA) was grafted onto poly(lactic acid) (PLA) in the presence of styrene (St) by using a free-radical grafting methodology. The grafting degree (Dg) of MA was increased from 0.65 wt % to 1.1 wt % with the St/MA ratio up to 2/1, where the grafting efficiency (Eg) of MA was 27%. However, both Dg and Eg were decreased with further increasing of the St/MA ratio to 4/1. The Dg of MA...
full textMechanical Properties of Polypropylene Coating Containing Maleic Anhydride on Plain Carbon Steel
Using Electrostatic Spray Coating Technique, Polypropylene Powder (EPD 60R) was applied on carbon steel substrates at room temperature. In order to obtain a uniform coating, steel substrates with powder coatings were heated in a vacuum oven at various temperatures up to 250° C for various periods of time up to 45 min and a pressure of 200 mb. The coatings produced had thicknesses of around 470 ...
full textMechanical Properties of Polypropylene Coating Containing Maleic Anhydride on Plain Carbon Steel
Using Electrostatic Spray Coating Technique, Polypropylene Powder (EPD 60R) was applied on carbon steel substrates at room temperature. In order to obtain a uniform coating, steel substrates with powder coatings were heated in a vacuum oven at various temperatures up to 250° C for various periods of time up to 45 min and a pressure of 200 mb. The coatings produced had thicknesses of around 470 ...
full textMy Resources
Journal title
volume 26 issue 1
pages 313- 322
publication date 2007-07
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023