Fatigue Life of Repaired Welded Tubular Joints

Authors

  • G. H. Farrahi School of Mechanical Engineering, Sharif University of Technology
  • N. Habibi Mechanical Engineering, University of Kurdistan
Abstract:

In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading.  It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened and repaired specimens is around 105%. The in depth residual stresses are measured on the repaired joints before and after fatigue loading. It can be stated that repair made a remarkable improvement into fatigue behaviour of tubular joints examined in this investigation. However, if repair is not possible, shot peening can be a good alternative to improve the fatigue life of welded joint but if repair is planned, shot peening may not be financially or technically justifiable.

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

Fatigue Life Prediction for Welded Joints with Known Initial Crack

The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...

full text

Fatigue Behaviour of Al 6082-T6 Friction Stir Welded Tubular Joints under Torsional Loading

The aim of the present research is to investigate the fatigue behaviour of friction stir (FS) welded tubular joints in aluminium alloy subjected to torsional fatigue loading. To manufacture the samples which were tested, an MTS I-STIR process development system was equipped with a retracting tool specifically designed for these tubular welds. Al 6082-T6 FS welded samples were tested under cycli...

full text

Fatigue Life Prediction of Rivet Joints

Strength reduction in structures like an aircraft could be resulted as cyclic loads over a period of time and is an important factor for structural life prediction. Service loads are emphasized at the regions of stress concentration, mostly at the connection of components. The initial flaw prompting the service life was expected by using the Equivalent Initial Flaw Size (EIFS) which has been re...

full text

Improving Fatigue Strength of Welded Joints by Ultrasonic Impact Treatment

Enhancement in fatigue performance of welded joints by Ultrasonic Impact Treatment (UIT) was evaluated with large-scale rolled beam and built-up specimens having yield strength of 345 to 760 MPa. Eighteen rolled-beam specimens having welded details at cover plates and transverse stiffeners and eight built-up specimens having only transverse stiffener details were fatigue tested after treating t...

full text

Fatigue Life Analysis of Crane K-Type Welded Joints Based on Non-Linear Cumulative Damage Theory

Engineering fatigue fracture failure is one of the most common phenomena of mechanical and structural failure, statistically representing approximately 50 to 90% of total mechanical damage [1]. Lattice structures have been widely used in crane booms, steel plants, parking garages, offshore platforms and other fields [2] to [4]. In a crane, the lattice boom has better mechanical properties compa...

full text

Effect of UIT on Fatigue Life in Web-Gusset Welded Joints

Ultrasonic impact treatment (UIT), which is a peening method, is usually used as a post-weld treatment in order to improve the fatigue strength of welded joints. In this study, fatigue tests were carried out on web-gusset welded joints treated by UIT and the results were compared with the fatigue lives of as-welded joints in order to examine the effects of UIT on the fatigue lives of welded joi...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 26  issue 1

pages  25- 32

publication date 2013-01-01

By following a journal you will be notified via email when a new issue of this journal is published.

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023