Fabrication of Nanostructured Cu matrix Nanocomposites by High Energy Mechanical Milling and Spark Plasma Sintering

Authors

  • Saeid Alipour Department of Materials Engineering, University of Maragheh
Abstract:

Spark plasma sintering (SPS) is a sintering process that is capable of sintering hard worked powders in short times. This technique was used to fabricate bulk Cu and Cu-SiC nanocomposites. Pure Cu and mixed powders of Cu including 4 vol% of SiC nanoparticles were mechanically alloyed for 25 h and sintered at 750˚C under vacuum condition by SPS method. Microstructures of the materials were characterized using optical and scanning electron microscopes and x-ray diffraction patterns, and mechanical properties were evaluated by micro hardness tests. The results showed density values of 8.69 and 8.30 g/cm3 and hardness values over 105 and 128Hv for Cu and its nanocomposite respectively. The addition of nanoparticles retarded Cu matrix grain growth during SPS process and resulted in higher hardness of nanocomposite compared to non-reinforced copper.

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

Characterization of In-Situ Cu–TiH2–C and Cu–Ti–C Nanocomposites Produced by Mechanical Milling and Spark Plasma Sintering

This study focuses on the fabrication and microstructural investigation of Cu–TiH2–C and Cu–Ti–C nanocomposites with different volume fractions (10% and 20%) of TiC. Two mixtures of powders were ball milled for 10 h, consequently consolidated by spark plasma sintering (SPS) at 900 and 1000 ◦C producing bulk materials with relative densities of 95–97%. The evolution process of TiC formation duri...

full text

ZrB2-CNTs Nanocomposites Fabricated by Spark Plasma Sintering

ZrB₂-based nanocomposites with and without carbon nanotubes (CNTs) as reinforcement were prepared at 1600 °C by spark plasma sintering. The effects of CNTs on the microstructure and mechanical properties of nano-ZrB₂ matrix composites were studied. The results indicated that adding CNTs can inhibit the abnormal grain growth of ZrB₂ grains and improve the fracture toughness of the composites. Th...

full text

Effect of High-Energy Ball Milling on the Magnetic Properties of NiZn Ferrite Ceramics Synthesized by Spark Plasma Sintering

High-density fine-grained Ni0.5Zn0.5Fe2O4 ferrite ceramics were synthesized by spark plasma sintering (SPS) in conjunction with high energy ball milling. The precursor powders were milled for 20 h, 40 h, and 60 h, respectively, and the milled powders were all sintered for 5 min at 900 ̊C. All the samples exhibit a single spinel phase. With increasing of the ball milling time, the relative densit...

full text

Nanocrystalline Al7075 + 1 wt % Zr Alloy Prepared Using Mechanical Milling and Spark Plasma Sintering

The microstructure, phase composition, and microhardness of both gas-atomized and mechanically milled powders of the Al7075 + 1 wt % Zr alloy were investigated. The gas-atomized powder exhibited a cellular microstructure (grain size of a few µm) with layers of intermetallic phases along the cell boundaries. Mechanical milling (400 revolutions per minute (RPM)/8 h) resulted in a grain size reduc...

full text

In-situ Fabrication of Transparent Magnesium Aluminate Spinel by Spark Plasma Sintering

Transparent polycrystalline spinel ceramic was fabricated without any sintering aids by spark plasma sintering method of a mixture of Al2O3 and MgO powders for only 10min soak at 1250°C. Densification, microstructure and optical transparency of spinel were examined. The spinel exhibits an in-line transmission of 55% for a visible-wavelength of 470nm and high hardness value of 2040 HV.

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 1  issue 3

pages  39- 43

publication date 2015-10-01

By following a journal you will be notified via email when a new issue of this journal is published.

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023