Fabrication and Characterization of Polyetherimide Hollow Fiber Membrane Contactor for Carbon Dioxide Stripping from Monoethanolamine Solution

Authors

  • S. Ali Asghar Hedayat Chemical Engineering Department, Mahshahr branch, Islamic Azad University, Mahshahr, Iran
  • Zabih A. Tarsa Chemical Engineering Department, Mahshahr branch, Islamic Azad University, Mahshahr, Iran
Abstract:

In this research, process asymmetric polyetherimide hollow fiber membranes using ethanol (0, 2 and 4 wt%) as non-solvent additive in the polymer dope via phase inversion method were fabricated. Aqueous solution of 1-methyl-2-pyrrolidine (NMP) (90%) was applied as a bore fluid to avoid inner skin layer formation and water was used as the external coagulant. The morphology of fabricated membranes was examined using field emission scanning electron microscope (FESEM). A gas permeation test was conducted using Nitrogen. Fabricated membranes were characterized in terms of pore size, critical water entry pressure, water contact angle and collapsing pressure. The performance of fabricated membranes for carbon dioxide stripping from monoethanolamine solution using a gas - liquid membrane contactor system was studied. The results showed that carbon dioxide stripping flux and efficiency increased by increasing liquid velocity. Also, enhancement of stripping flux by increasing gas velocity was negligible. By increasing MEA solution temperature, stripping flux increased; therefore, liquid phase temperature is a key parameter which needs to be controlled.

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

fabrication and characterization of polyetherimide hollow fiber membrane contactor for carbon dioxide stripping from monoethanolamine solution

in this research, process asymmetric polyetherimide hollow fiber membranes using ethanol (0, 2 and 4 wt%) as non-solvent additive in the polymer dope via phase inversion method were fabricated. aqueous solution of 1-methyl-2-pyrrolidine (nmp) (90%) was applied as a bore fluid to avoid inner skin layer formation and water was used as the external coagulant. the morphology of fabricated membranes...

full text

Polyvinylidene Fluoride Hollow Fiber Membrane Contactor Incorporating Surface Modifying Macromolecule for Carbon Dioxide Stripping from Water

Porous surface modified polyvinylidene ï‌‚uoride (PVDF) hollow fiber membranes are fabricated through a dry-wet phased inversion process. Surface modifying macromolecules (SMM) (1 wt. %) are used as additives in the spinning dope. The performance of the surface modified membrane in contactor application for CO2 stripping from water is assessed through the fabricated gas–liquid membrane contacto...

full text

Influence of Air-Gap Length on CO2 Stripping from Diethanolamine Solution and Water Performance of Surface Modified PVDF Hollow Fiber Membrane Contactor

Surface Modifying Macromolecule (SMM) blended PVDF hollow fibers (HFs) were spun at different air-gaps (o to 20 cm) and used for CO2 stripping from aqueous DEA solution and water. The manufactured fibers were first subjected to various characterization tests such as contact angle and critical water entry pressure measurement to evaluate the HF hydrophobicity and wetting resistanc...

full text

Separation and Fixation of Carbon Dioxide Using Polymeric Membrane Contactor

Polypropylene hollow fiber membrane (PPHFM) contactor, with aqueous solution absorbent such as sodium hydroxide (NaOH), monoethanolamine (MEA) and diethanolamine (DEA), was designed and used to separate and fix CO2 from CO2/N2 gas mixtures. The factors that influence the separation properties of CO2/N2 were investigated. It was found that the CO2 removal efficiency is the best by using MEA solu...

full text

Effect of Ethylene Glycol as Pore Former on Polyphenylsulfone Hollow Fiber Membrane for Crude Palm Oil Deacidification through Membrane Contactor

In this study, polyphenylsulfone (PPSU) hollow fiber membrane was fabricated via a wet spinning method with the addition of ethylene glycol (EG) in the range of 0-10 wt% as the additive. The EG was added to improve the membrane pore formation and interconnectivity for better membrane contactor performance in extracting and removing the free fatty acid (FFA) from crude palm oil (CPO). Four diffe...

full text

Fabrication of Crosslinkable Hollow Fiber Membranes for Pervaporation Dehydration

Integrally-skinned asymmetric Polyetherimide/Poly (vinyl alcohol) (PEI/PVA) hollow fber membranes for pervaporation dehydration were fabricated by non-solvent induced phase inversion. PVA inside the PEI matrix could be crosslinked to provide membrane performance stability during long term operation. The effects of different PEI/PVA blend ratio, external coagulant type and...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 1  issue 3

pages  118- 123

publication date 2015-10-01

By following a journal you will be notified via email when a new issue of this journal is published.

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023