EFFECT OF POST-DEFORMATION ANNEALING TREATMENT ON INTERFACE PROPERTIES AND SHEAR BOND STRENGTH OF Al-Cu BIMETALLIC RODS PRODUCED BY EQUAL CHANNEL ANGULAR PRESSING

Authors

Abstract:

Effects of annealing treatment after equal channel angular pressing (ECAP) on the interface properties and shear bond strength of Al/Cu bimetallic rods were investigated. For the as-deformed samples, the one with two passes of ECAP indicated higher shear bond strength. Formation of a layer of intermetallic compounds after annealing treatment is confirmed. In general, by increasing annealing temperature, thickness of intermetallic compounds at the interface increases. Shear bond strength was initially reduced by annealing at 200, 250 and 300 ͦ C and increased at 350 ͦ C. With further increase in annealing temperature to 400 ͦ C, shear bond strength slightly decreased which is correlated to the increased thickness of the intermetallic compounds.

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

Modeling and production of high strength Al strips by equal channel multi angular pressing method

Equal channel multi angular pressing (ECMAP) process is the efficient method to enhance the productivity of ultra-fine grained (UFG) materials, by increasing process continuity and as a result decreasing process required time. Comparing repetitive ECAP method, in the same period, the number of passes can be done by ECMAP. In this article, ECMAP of AL strips in two typical annealed and as receiv...

full text

Effect of Equal Channel Angular Pressing and Annealing Treatment on the Evolution of Microstructure in AlMg0.7Si Aluminum Alloy

In this research, samples of AlMg0.7Si aluminum alloy are deformed up to three passes using equal channel angular pressing (ECAP). Formation of a sub-micron structure after three passes of ECAP is demonstrated. Microstructural stability of the samples is investigated at temperatures of 300-500 °C. At 300 °C, fine recrystallized structure forms after 10 min which remains stable when the ...

full text

Hot and Cold Tensile Behavior of Al 6061 Produced by Equal Channel Angular Pressing and Subsequent Cold Rolling

The full annealing AA6061 aluminum alloy was subjected to severe plastic deformationvia the combination of equal channel angular pressing (ECAP) and cold rolling (CR) in order torefine its microstructure and to improve its mechanical properties. According to the results of hotand cold tensile tests, the combination of ECAP and CR significantly affected the final strengthand ductility of studied...

full text

Size effect in equal channel angular pressing (ECAP) process

The influence of the sample size (diameter while keeping the length constant) in equal channel angular pressing (ECAP) of pure aluminum is examined using finite element method (FEM) and experiment. Different sized aluminum rods were processed via ECAP and the effect of sample size on the strain homogeneity, process load, and the ratio of the friction to the total force were evaluated. The resul...

full text

Ten years of severe plastic deformation (SPD) in Iran, part I: equal channel angular pressing (ECAP)

The superior properties of ultrafine-grained materials fabricated by severe plastic deformation (SPD) have attracted the attention of many researchers around the world.  Among the top-ranked countries that are active in this field, Iran is interesting because of the late beginnings of SPD in this country and, subsequently, the highest rate of growth in the number of publications during the last...

full text

Achieving microstructures prone to superplastic deformation in an Al - Zn - Mg - Cu alloy by equal channel angular pressing

An Al-Zn-Mg-Cu alloy without Sc or Zr additions was subjected to overaging and processing by equal channel angular pressing, obtaining a grain size of ∼160 nm and a fraction of high-angle boundaries of 56%. The high elongations attained at high strain rate (10-10 s) and low test temperature (250-300 oC) are attributed to the formation of new recrystallized grains, ∼500 nm in size, during heatin...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 14  issue 4

pages  25- 34

publication date 2017-12

By following a journal you will be notified via email when a new issue of this journal is published.

Keywords

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023