Dynamic recrystallization kinetics of AISI 403 stainless steel using hot compression test

Authors

  • A. Momeni Department of Materials Science and Engineering, Hamedan University of Technology, Hamedan, Iran
  • E. Kevanlo Department of Materials and Polymer Engineering, Hakim Sabzevari University, Sabzevar, Iran
  • S.A.A. Sani Department of Materials Science and Engineering, Iran University of Sience and Technology, Tehran, Iran
Abstract:

In this work dynamic recrystallization behavior of AISI 403 martensitic stainless steel was studied using hot compression tests over temperature range of 900 C -1200 C and strain rate range of 0.001 s-1 - 1 s-1. The obtained flow curves showed that the hot compression behavior of the alloy is controlled by dynamic recrystallization. The flow stress and strain corresponding to the critical, peak and onset of steady state region were related to the Zener-Hollomon parameter using simple power equations. The variation of dynamic recrystallization fraction with strain showed that restoration kinetics is enhanced with increasing temperature and decreasing strain rate. The development of DRX was modeled using Avrami Kinetics equation. The equations proposed by Baragar and Cingara-McQueen were used to develop a new model capable of predicting the flow curves up to the onset of steady state flow region. This work softening is mainly controlled by the phenomenon dynamic recrystallization.

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

dynamic recrystallization kinetics of aisi 403 stainless steel using hot compression test

in this work dynamic recrystallization behavior of aisi 403 martensitic stainless steel was studied using hot compression tests over temperature range of 900 c -1200 c and strain rate range of 0.001 s-1 - 1 s-1. the obtained flow curves showed that the hot compression behavior of the alloy is controlled by dynamic recrystallization. the flow stress and strain corresponding to the critical, pe...

full text

Dynamic Recrystallization under Hot Deformation of a PH Stainless Steel

Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...

full text

Dynamic Recrystallization and Hot Workability of 316LN Stainless Steel

Chaoyang Sun 1,*, Yu Xiang 1, Qingjun Zhou 2, Denis J. Politis 3, Zhihui Sun 1,* and Mengqi Wang 1 1 School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China; [email protected] (Y.X.); [email protected] (M.W.) 2 Capital Aerospace Machinery Company, Beijing 100076, China; [email protected] 3 Department of Mechanical Engineering, Imperial Co...

full text

dynamic recrystallization under hot deformation of a ph stainless steel

dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...

full text

Dynamic Recrystallization by Necklace Mechanism During Hot Deformation of 316 Stainless Steel

The aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (DRX). The material used is 316 stainless steel. In order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of 950-1100 °C with strain rates of 0.01-1s-1. The result shows that at the tempera...

full text

dynamic recrystallization by necklace mechanism during hot deformation of 316 stainless steel

the aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (drx). the material used is 316 stainless steel. in order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of 950-1100 °c with strain rates of 0.01-1s-1. the result shows that at the temperature of 100...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 1  issue Issue 2

pages  32- 43

publication date 2014-10-01

By following a journal you will be notified via email when a new issue of this journal is published.

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023