Bimetal friction stir welding of aluminum to magnesium

Authors

  • H.A Mehrabi Department of materials science and engineering, Karaj Branch, Islamic Azad University, Iran
  • M Abbasi Department of materials science and engineering, Karaj Branch, Islamic Azad University, Iran
  • P Pourahmad Department of materials science and engineering, Karaj Branch, Islamic Azad University, Iran
Abstract:

FSW material flow and phase transformation were studied at the interface of dissimilar welding of Al 6013 to Mg. Defect free butt weld was obtained when aluminum and magnesium test plates were placed in the advancing side and retreating side respectively, and the tool was placed 1 mm off the weld centerline into the aluminum side. In order to understand how the materials flow during FSW, steel shots were implanted as indexes into the test plate’s intimate face and welding was performed with determined optimum parameters. X-ray images were used to evaluate secondary positions of the steel shots at weld zone. It was revealed that steel shots implanted in the advancing side test plate were penetrated from advancing side into the retreating side with a relatively large rotational displacement of α. But shots implanted in retreating side test plate remained only in retreating side, without penetrating into the advancing side, and displaced by a low angle of β. It could be concluded that to reach defect free welds by FSW between two dissimilar metals, the tool should be inserted in harder metal and harder metal should be placed in the advancing side too. EDS analysis was performed in order to study formation and distribution of intermetallic phases in the welds interface. Two intermetallic compounds formed sequentially at Al6013/Mg interface were Al3Mg2 and Al12Mg17 in weld condition. Welded specimens were heat treated and their effects on mechanical properties of welds and formation of new intermetallic layers were investigated.

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

Analysis and Comparison of Friction Stir Welding and Laser Assisted Friction Stir Welding of Aluminum Alloy

Friction Stir Welding (FSW) is a solid-state joining process; i.e., no melting occurs. The welding process is promoted by the rotation and translation of an axis-symmetric non-consumable tool along the weld centerline. Thus, the FSW process is performed at much lower temperatures than conventional fusion welding, nevertheless it has some disadvantages. Laser Assisted Friction Stir Welding (LAFS...

full text

On the Characteristics of Friction Stir Welding Lap Joint of Magnesium and Aluminum

Lap joints of commercially pure magnesium plates to aluminium plates (Magnesium plate on the top, and Aluminium plate, grade 1100, on the bottom side) were conducted by friction stir welding using various traveling and rotation speeds of the tool to investigate the effects of the welding parameters on the joint characteristics and strength. Defect-free lap joints were obtained in the welding tr...

full text

Liquation Cracking of Dissimilar Aluminum Alloys during Friction Stir Welding

A liquation cracking mechanism of dissimilar Al alloys during the friction stir welding (FSW) is suggested in this study. To identify the mechanism, the precipitates were analyzed and Al-Mg-Cu phase diagrams were calculated. Electron backscattering diffraction (EBSD) analysis and electron probe microanalysis (EPMA) were also conducted. In the same manner as constitutional liquation, at high hea...

full text

Friction Stir Welding of Aluminum Alloys: A Review

Friction stir welding is a solid state joining process. High strength aluminum alloys are widely used in aircraft and marine industries. Generally, the mechanical properties of fusion welded aluminum joints are poor. As friction stir welding occurs in solid state, no solidification structures are created thereby eliminating the brittle and eutectic phases common in fusion welding of high streng...

full text

Friction stir welding and processing

Friction stir welding (FSW) is a relatively new solid-state joining process. This joining technique is energy efficient, environment friendly, and versatile. In particular, it can be used to join high-strength aerospace aluminum alloys and other metallic alloys that are hard to weld by conventional fusion welding. FSW is considered to be the most significant development in metal joining in a de...

full text

Review: friction stir welding tools

Friction stir welding (FSW) is a widely used solid state joining process for soft materials such as aluminium alloys because it avoids many of the common problems of fusion welding. Commercial feasibility of the FSW process for harder alloys such as steels and titanium alloys awaits the development of cost effective and durable tools which lead to structurally sound welds consistently. Material...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 1  issue 1

pages  27- 38

publication date 2013-01-01

By following a journal you will be notified via email when a new issue of this journal is published.

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023