سنتز پودر نانوکامپوزیت Al2O3-TiN توسط مکانوشیمیایی
Authors
Abstract:
In recent years, much research in the field of advanced materials synthesis using the mechanochemical process has been performed. In this study, Al2O3-TiN nanocomposite was produced by the mechanochemical method and using inexpensive material TiO2 (instead of pure titanium which is too expensive). Also, aluminum and titanium oxide powders were used as raw materials. Milling under N2 atmosphere with 5 atmospheric pressure was performed and the products were evaluated by the SEM and XRD. Milling results showed that in the first stage of the synthesis process, titanium oxide is reduced by aluminum and the process continues, producing titanium reaction with nitrogen. When the Al/TiO2 ratio molar is equal to 1.2 and 1.3, after 20 hours of milling, TiN peaks in the XRD appears. Moreover, the results showed that milling leads to the formation of fine and spherical particles.
similar resources
سنتز پودر نانوکامپوزیت al۲o۳-tin توسط مکانوشیمیایی
درسالهای اخیر، تحقیقات زیادی در زمینه استفاده از فرایند مکانوشیمیایی برای سنتز مواد پیشرفته صورت گرفته است. در این تحقیق، نانوکامپوزیت al2o3-tin به روش مکانوشیمیایی و با استفاده از ماده ارزان قیمت tio2 (به جای تیتانیوم خالص که خیلی گران است) تولید شد. از پودرهای اکسید تیتانیوم و آلومینیوم به عنوان مواد اولیه استفاده شد. آسیابکاری در آتمسفر نیتروژن با فشار 5 آتمسفر انجام شد و محصولات به دست آمده...
full textسنتز نانوکامپوزیت al2o3/mo از اکسید مولیبدن به روش مکانوشیمیایی
مواد نانو کامپوزیت به خاطر ریز دانه بودن و وجود فصل مشترک فوق العاده زیاد، دارای کسر زیادی از اتم ها در مرزدانه ها بوده، به طوری که خواص قابل توجهی را در مقایسه با سایر مواد از خود بروز می دهند. فرآیند های مختلفی همچون ذوب و ریخته گری و یا انجماد سریع و فرآیندهای مکانوشیمیایی برای تولید نانوکامپوزیت ها وجود دارند. قابلیت های منحصر به فرد روش مکانوشیمیایی مانند؛ انجام واکنش ها در حالت جامد، تهیه...
15 صفحه اولاثر زمان آسیابکاری بر تولید نانوکامپوزیت زمینه سرامیکی TixAly/Al2O3 به روش مکانوشیمیایی
In recent years, much research has been performed in the field of nanomaterials synthesis using mechanochemical process. In this research, TixAly/Al2O3 ceramic matrix nanocomposite was produced by the mechanochemical method. Aluminum and inexpensive titanium oxide powders were used as raw materials, and milling was performed under N2 atmosphere. The results showed that reduction of TiO2 by Al i...
full textبررسی تأثیر سرعت آسیاکاری بر تولید نانوکامپوزیت درجای Al2O3-ZrB2 با استفاده از روش مکانوشیمیایی
در این پژوهش اثر سرعت آسیاکاری بر سامانه احتراقی Al/ZrO2/H3BO3مورد بررسی قرار گرفت. بدین منظور پودرهای خام اولیه با نسبتهای استوکیومتری مشخص و نسبت گلوله به پودر 1:10 با سرعتهای350، 450 و500 دور بر دقیقه به مدت 15 ساعت تحت عملیات آسیاکاری قرار گرفتند. همچنین، آنالیز حرارتی افتراقی(DSC ) با نرخ گرمایش°C/min 40 بر روی نمونهها انجام شد. بمنظور بررسی فازهای تشکیل شده، آنالیز فازی XRD بر روی...
full textساخت نانوکامپوزیت پایه سرامیکی al2o3-zrb2 به دو روش سنتز مکانوشیمیایی و سنتز دمای بالای خودپیشرونده
در این پژوهش امکان ساخت کامپوزیت سرامیکی al2o3-zrb2 به دو روش سنتز احتراقی و سنتز مکانوشیمیایی مورد بررسی قرار گرفت. به منظور افزایش تمایل واکنش دهنده ها به سنتز احتراقی، پودرها قبل از فرآیند سنتز، به وسیله آسیا، تحت عملیات فعال سازی مکانیکی قرار گرفتند. با استفاده از آنالیز حرارتی افتراقی اثر سرعت و زمان آسیاکاری بر دمای شروع احتراق و همچنین شدت واکنش ها در مخلوط پودری بررسی شد. نتایج آنالیز ح...
My Resources
Journal title
volume 30 issue 2
pages 13- 22
publication date 2011-12
By following a journal you will be notified via email when a new issue of this journal is published.
No Keywords
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023