ساخت نانو بلورک‌های δ-7O3Cu2YBa به روش مکانوشیمیایی و بررسی دمای گذار ترکیبات -7O3Cu2YBa(x-1) + 2 xMnO (02/0 ،015/0 ،01/0 ،005/0 ،0 = x)

Authors

  • بهدانی, محمد آزمایشگاه تحقیقاتی حالت جامد
  • تجبر, ناصر آزمایشگاه تحقیقاتی حالت جامد
  • یزدانیان, سمیه آزمایشگاه تحقیقاتی حالت جامد
Abstract:

In this research, YBa2Cu3O7-d (0 < d < 1) nanocrystalite superconductor was prepared by mechanochemical alloying method. We synthesized YBa2Cu3O7-d via mixing the BaCO3, Y2O3, CuO powders and milling in SPEX 8000 for 5h with weight ratio of ball to powder 10:1 and steel balls of 11mm diameter, followed by heating for 4h at 850 ˚C. The superconductor phase formation process was completed with sintering treatment under oxygen partial pressures.The superconducting transition temperature of the samples was investigated using the four-probe method. Then transition temperature of xMnO2 + (1-x) YBa2Cu3O7-d compounds was studied. The superconducting transition temperature of the final samples with x = 0, 0.005, 0.01 is found to be 83 K, and for the samples with x > 0.015, the superconductivity was vanished.ر

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

ساخت نانو بلورک های δ-۷o۳cu۲yba به روش مکانوشیمیایی و بررسی دمای گذار ترکیبات -۷o۳cu۲yba(x-۱) + ۲ xmno (۰۲/۰ ،۰۱۵/۰ ،۰۱/۰ ،۰۰۵/۰ ،۰ = x)

در این پژوهش نانو بلورک­های ابررسانای δ-7o3cu2yba )1 > d >0)، به روش مکانوشیمیایی ساخته شدند. این ترکیب با استفاده از پودرهای 3baco، 3o2y، cuo پس از 5 ساعت آسیاکاری در دستگاه آسیای spex 8000  با نسبت وزنی ده به یک گلوله به پودر و گلوله های فولادی به قطر  mm11 و سپس گرمادهی به مدت 4 ساعت در دمایoc 850 شکل گرفت. به منظور تشکیل کاملتر فاز ابررسانا، مرحله­ی تفجوشی همراه با اکسی‍ژن­دهی روی نمونه­ها ...

full text

ساخت ابررسانای yba2cu3o7-δ به روش آلیاژسازی مکانوشیمیایی و بررسی اثر ناخالصی mno2 بر دمای گذار آن

دراین تحقیق ساخت ابررسانای δ-7o3cu2yba )1 > δ >0) به روش های آلیاژسازی مکانیکی و مکانوشیمیایی بررسی شد. این ترکیب به روش آلیاژسازی مکانیکی با استفاده از پودرهای 3baco، 3o2y، cuo پس از 32 ساعت آسیاکاری در دستگاه آسیای 8000spex با نسبت وزنی گلوله به پودر 10:1 و گلوله های فولادی به قطر mm11 ساخته نشد ولی در روش آلیاژسازی مکانوشیمیایی با استفاده از همان پودرها پس از 5 ساعت آسیاکاری در دستگاه آسیای ...

بررسی فازی ترکیبات Mo + 2(1 - x) Si + 2xAl

X-ray powder diffraction data for Mo2.85Al1.91Si4.81 are presented here. The new Mo2.85Al1.91Si4.81 compound was successfully prepared, using the self-propagating high-temperature synthesis (SHS) technique. The starting atomic mixture of reactant powders was Mo + 2(1 - x)Si + 2xAl with 0.2 ≤ x ≤ 0.5. The final powder compound obtained by the SHS technique was determined to be in x = 0.2; Mo(Si,...

full text

بررسی‌های ساختاری و مغناطیسی نانوذرات‌ پروسکایت LaMn1-xCoxO3 (0/1، 75/0، 5/0، 25/0، 0/0 = x)

In this work, the structural and magnetic properties of LaMn1-xCoxO3 (x = 0.00, 0.25, 0.50, 0.75, 1.00) are investigated. The structural characterization of compounds by X-ray powder diffraction is evidence for a rhombohedral structure (R -3c space group). Much less increase of the unit cell volume suggests that Co enters in lattice as Co+2 for x ≤ 0.5 while much more decrease of the unit cell ...

full text

مطالعه خواص مغناطیسی و الکتریکی نانو فریت های 4o2fe x cu (x- 5/0)mn 5/0 ni (5/0 ، 3/0 ،1/0 ، 0/0=x )

نانوذرات مغناطیسی فریت نیکل- منگنز- مس عمدتأ در دارورسانی مغناطیسی، محیط های مغناطیسی ضبط داده ها، حسگرهای گازی، مدارهای فرکانس بالا و ذخیره اطلاعات و ... کاربرد فراوانی دارند. در این پایان نامه نانوذرات مغناطیسی فریت نیکل - منگنز - مس با درصدهای متفاوت جانشانی مس به جای منگنز به روش هم رسوبی شیمیایی تهیه شدند و خواص ساختاری، مغناطیسی و الکتریکی آنها مورد مطالعه و بررسی قرارگرفت. برای مشخصه یاب...

تولید درجای نانو کامپوزیت Cu-Cr)-Al2O3) به روش مکانوشیمیایی

در این پژوهش، نانوکامپوزیت Cu-Cr/Al2O3 به روش مکانوشیمیایی و از مخلوط اولیه ی CuO، Al ،Cu و Cr2O3 با درصدهای گوناگون و با استفاده از آسیاکاری پر انرژی تولید شد. اساس تولید این نانوکامپوزیت واکنش های احیایی بود. به گونه ای که در حین فرایند اکسیدهای کرم و مس به وسیله ی آلومینیوم احیاء شده و محصول نهایی یک کامپوزیت زمینه فلزی شامل محلول فوق اشباع کرم در مس به عنوان زمینه و اکسید آلومینیوم به عنوان...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 19  issue 2

pages  219- 226

publication date 2011-07

By following a journal you will be notified via email when a new issue of this journal is published.

Keywords

No Keywords

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023