Plastic bonded explosive PBXN-103 as an underwater charge based on energetic binder system uses in warhead section of several navy weapons. Metriol trinitrate (MTN), triethylene glycol dinitrate (TEGDN) and pelletized nitrocellulose are basic ingredients of binder system in PBXN-103 formulation. In this research the effects of applying accessible Poly glycidyl nitrate (PGN) as binder, were investigated on physical, mechanical, thermal, and sensitivity properties of PBXN-103. Results were indicated that the binder replacement enhanced obviously the tensile strength and elongation to 85 psi and 70 % respectively. Based on differential scanning calorimetry (DSC), the thermal stability of formulation was increased 20 °C in comparison with PBXN-103 and reached to 190 °C. Glass transition temperature, vacuum thermal stability, impact sensitivity and friction sensitivity were -54 °C and 4.06 ml/g/48h, 7 N.m and 7.2 kg.F respectively. This new formulation was not fired by exploding No. 8 commercial electric detonator.
similar resources
اثر نرم‌کننده‌های مختلف بر خواص ماده منفجره زیرآبی PBXN-111
PBXN-111 is a common plastic bonded explosive has been widely used in warhead section of several navy weapons. This charge is based on HTPB resin and prepared with cast-cure method. Isodecyl pelargonate (IDP) as plasticizer is used in PBXN-111 formulation. Considering limitations to prepare IDP, in this research the effect of replacement of dioctyl adipate (DOA) and dioctyl sebacate (DOS) inste...
full textپارامترهای تجزیه حرارتی ماده منفجره پلاستیکی PBXN-111
PBXN-111 is a cast cured underwater explosive containing RDX, ammonium perchlorate, aluminium powder and HTPB binder. In this research, the kinetics and thermodynamic properties of thermal decomposition of this PBX investigated by Kissinger and Flynn-Wall-Ozawa (FWO) methods based on differential scanning calorimetry under non-isothermal condition with heating rate of 5, 10, 15 and 20 °C/mi...
full textبررسی اثر نسبت NCO/OH بر خواص مکانیکی ماده منفجره پلاستیکی PBXN-109(علمی-پژوهشی)
The aim of this research is improvement of elongation at break of PBXN-109 polymer bonded explosive. Due to the great effect of isocyanate/hydroxyl ratio (r=NCO/OH) on mechanical properties of plastic bonded explosives, in this research, the samples of PBXN-109 with different r-values of 1, 0.95, 0.85, 0.75 and 0.65 were prepared and analyzed by hardness and tensile tests. The results show that...
full textبررسی اثر نسبت nco/oh بر خواص مکانیکی ماده منفجره پلاستیکی pbxn-۱۰۹(علمی-پژوهشی)
هدف این مقاله بهبود خاصیت ازدیاد طول در شکست ماده منفجره پلاستیکی pbxn-109 می باشد. با توجه به تاثیر نسبت گروه های ایزوسیانات به هیدروکسیل (r=nco/oh) در تعیین خواص مکانیکی مواد منفجره پلاستیکی، در این تحقیق نمونه های مختلف با نسبت گروه های ایزوسیانات به هیدروکسیل برابر 1، 95/0، 85/0، 75/0 و 65/0 تهیه شده و تحت آزمون های کشش و سختی قرار گرفتند. نتایج آزمایشات نشان دادند که در نسبت 65/0r= و کمتر،...
full textسنتز و فرمولاسیون سیستم بایندر- نرم کننده nhtpb-npb و بررسی خواص عملکردی آن در pbxn-۱۰۹ اصلاح شده
در این تحقیق نیتراسیون پلی بوتادیان (pb) با وزن مولکولی پایین، از طریق یک روش معمول و ارزان انجام شد. محصول npb (نیترو پلی بوتادیان) توسط تکنیکهای ft-ir، 1h-nmr، gpc، tga، dsc و ... مورد بررسی قرار گرفت. سپس نرمکننده پلیمری پرانرژی npb به همراه بایندر پلی بوتادیان نیترهشده و خاتمهیافته با هیدروکسیل (nhtpb) به ترتیب جایگزین نرمکننده خنثی دی اکتیل آدیپات (doa) و بایندر پلی بوتادیان خاتمه...
full textMy Resources
Journal title
volume 14 issue 2
pages 62- 72
publication date 2019-06
By following a journal you will be notified via email when a new issue of this journal is published.
No Keywords
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023