بررسی کهولت پیشرانه‌ی جامد مرکب بر پایه‌ی HTPB با استفاده از روش وان‌هوف
Authors
Abstract:
In this article the aging of HTPB based composite solid propellants have been studied by Van’t Hoff method. The F-factor of Van’t Hoff equation was calculated by dynamic mechanical analysis (DMA) for reference propellants sample that was equal 2.5. Then the accelerated aging program conditions have been determined by Van’t Hoff equation. According to accelerated aging program the reference propellant samples subjected temperature range between 25°C and 80°C so that the aging time equal 2 years at 25°C. The change in dynamic mechanical properties, including the storage modulus (E') and loss factor or damping efficiency (tanδ) with time and temperature was used to assessment the aging behaviour of composite solid propellant. The result showed that storage module increased with time whereas loss factor decreased.
similar resources
بررسی کهولت پیشرانههای جامد مرکب برپایه HTPB
کهولت پیشرانههای جامد مرکب برپایه‌ی HTPB بررسی می‌شود که یکی از پارامترهای اصلی در ارزیابی طول‌عمر پیشرانههای مورد استفاده در سامانه‌های راکتی و موشکی به‌شمار می‌آید. امروزه پیشرانههای جامد مرکب بر پایه‌ی HTPB کارآمدترین پیشرانه برای کاربرد در موتورهای پیشرانه جامد در سراسر جهان هستند. فرایندهای کهولت پیشرانههای جامد مرکب می‌تواند پیامد فرایندهای شیمیایی، فیزیکی و مکانیکی باشد. در این مقال...
full textبررسی تاثیر ریزساختار HTPB بر کهولت پیشرانه جامد مرکب با استفاده از آزمون دینامیکی مکانیکی
In this article aging behavior of composite solid propellant was investigated by determining its mechanical properties at elevated temperatures. For this purpose, three HTPB samples with different microstructures were selected and composite solid propellants were prepared based on them keeping similar other components and aging was studied by accelerated method. Mechanical properties were meas...
full textبررسی پارامترهای موثر بر کهولت پیشرانههای جامد مرکب بر پایه‌ی HTPB
HTPB based composite Solid propellants are the source of power for the propulsion of rockets and missiles. Since composite solid rocket propellants, used in rockets and missiles is the fastest degrading component of the complete system, shelf life of the system is mainly governed by the life of the propellants. During storage and transportation, the propellant grains are subjected to various co...
full textبررسی پارامترهای موثر بر کهولت پیشرانه های جامد مرکب بر پایه ی htpb
پیشرانه های جامد مرکب بر پایه ی htpb منبع انرژی برای پیشرانش راکت ها و موشک ها می باشند. از آنجایی که پیشرانه های جامد مورد استفاده در سامانه های راکتی و موشکی با سرعت بیشتری نسبت به دیگر اجزای سیستم دچار تخریب می شوند لذا طول عمر کل سیستم عمدتاً به وسیله ی عمر پیشرانه ها تعیین می شود. گرین های پیشرانه در موقع انبارداری و حمل و نقل در معرض عوامل محیطی مختلفی همچون رطوبت، دما، ارتعاش و شوک قرار ...
full textمقایسه خواص پیشرانههای جامد مرکب بر پایه HTPB و NHTPB/HTPB
Hydroxyl terminated polybutadiene (HTPB) is the most commonly used binder in composite solid propellants. However, due to its non-energetic character, in practice it is just a dead weight; Therefore, replacing HTPB with an energetic polymer is essential. In this research, nitrated hydroxyl terminated polybutadiene resin (NHTPB) with 12.2% nitration rate, in combination with HTPB resin was used ...
full textMy Resources
Journal title
volume 13 issue 1
pages 63- 71
publication date 2019-03
By following a journal you will be notified via email when a new issue of this journal is published.
No Keywords
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023