بررسی خواص ساختاری و مغناطیسی الیاف ابررسانای YBa2Cu3O7- ساخته شده به‌روش الکتروریسندگی
Authors
Abstract:
Electrospinning is one of the most feasible techniques for producing nanoceramic fibers. In this paper, YBa2Cu3O7-δ (YBCO) superconductor nanofibers synthesized using electrospinning. The first step was preparation of a composite that is formed by mixing yttrium, barium, and copper acetates with different percent of polyvinyl alcohol (PVA). Then, the composite polymer has been electrospun to produce nanofibers. In order to obtain the calcination temperature, thermograviation analysis has been employed. Finally, for characterization, the nanofibers samples have been studied by, SEM, XRD, and ac magnetic susceptibility before and after sintering. The results showed that the best fibers in terms of diameter size and the absence of bead defects are attributed to 7.5 wt% of acetates. Also, the best sintering temperature for synthesizing the fiber sample of YBa2Cu3O7-δ was found 930 °C and the transition temperature of the fiber sample was obtained 93.2 K.
similar resources
خواص مغناطیسی و ساختاری ابررسانای 2223- Bi آلاییده با کادمیوم
In this paper, Bi1.64-xPb0.36CdxSr2Ca2Cu3Oy (BPCSCCO) superconductor with x = 0.0, 0.02, 0.04 and 0.06 is made by the solid state reaction method. The magnetic susceptibility measurements were performed using AC susceptometer. The microstructure and morphology of the samples have been studied by X-ray diffraction, scanning electron microscope and energy dispersive X-ray. The results show that t...
full textخواص مغناطیسی و ساختاری ابررسانای ۲۲۲۳- bi آلاییده با کادمیوم
در این مقاله ابررسانای bpcscco)) bi1.64-xpb0.36cdxsr2ca2cu3oy که در آن x=0.0, 0.02, 0.04, 0.06 می باشد به روش واکنش حالت جامد تهیه گردید. پذیرفتاری مغناطیسی نمونه ها اندازه گیری شده و ساختار آنها توسط xrd، sem و edx مورد مطالعه قرار گرفته است. اگرچه وجود سرب برای تشکیل فاز bi-2223 ضروری بوده، اما حضور کادمیوم به ایجاد درصد بالای فاز مذکور و پایداری آن کمک می کند. نتایج حاصل از الگوهای پراش و پذ...
full textتأثیر pH بر خواص ساختاری و مغناطیسی نانوذرات PbFe12O19 ساخته شده به روش سل- ژل
In this research, lead hexaferrites nanoparticles (PbFe12O19) were prepared by sol-gel method. The effect of pH on the structural and magnetic properties of PbFe12O19 was studied. The attempt in this paper was to depict the effect of change in sol-gel pH on the size and morphology of the samples as well as their structural and magnetic properties. Therefore, samples with pH = 1.8, 3, 5, 6, 7, a...
full textتأثیر آلایش نقره بر خواص ساختاری، الکتریکی و مغناطیسی سیم ابررسانای Bi/Ag 2223
In this study, the superconducting properties of Bi-2223/Ag wires, made by the PIT method have been studied. Powder samples were prepared using conventional solid state reaction method. After calcination, samples with different Ag percent (0, 5, 10, 15, 20, and 25) prepared and sintered at 830 °C. It was shown that Ag addition has not only affected the formation of the desired Bi-2223 phase an...
full textساخت و بررسی فیبر و نانوفیبر ابررسانای سرامیکی yba2cu3o7-? به روش الکتروریسندگی
یکی از روش های بسیار کارآمد برای ساخت نانوفیبرها روش الکتروریسندگی است. با ساخت اولین نانوفیبرسرامیکی در سال 2002 با این روش، افق جدیدی برای ساخت نانوفیبرهای سرامیکی از جمله نانوفیبرهای ابررساناهای دمای بالا باز شد. این روش به طورکلی شامل 3 مرحله است: 1) تهیه ی یک سل مناسب از پیش مواد غیرآلی و پلیمری 2) الکتروریسندگی محلول و به دست آوردن فیبرهای ترکیبی3) پخت فیبرهای به دست آمده در دمای مناسب. د...
15 صفحه اولMy Resources
Journal title
volume 26 issue 4
pages 1037- 1050
publication date 2019-01
By following a journal you will be notified via email when a new issue of this journal is published.
No Keywords
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023