بررسی اثر نسبت NCO/OH بر خواص مکانیکی ماده منفجره پلاستیکی PBXN-109(علمی-پژوهشی)
Authors
Abstract:
The aim of this research is improvement of elongation at break of PBXN-109 polymer bonded explosive. Due to the great effect of isocyanate/hydroxyl ratio (r=NCO/OH) on mechanical properties of plastic bonded explosives, in this research, the samples of PBXN-109 with different r-values of 1, 0.95, 0.85, 0.75 and 0.65 were prepared and analyzed by hardness and tensile tests. The results show that sample with r-value of 0.65 does not cure, completely. Besides, with decrement of r-value, the elongation at break of PBXN-109 increases, and tensile strength and stiffness decrease. The results of elongation at break for samples containing r-values of 1, 0.95, 0.85 and 0.75 are 8.46, 10.99, 11.64 and 26.63, respectively. According to this research, PBXN-109 with the r-value of 0.8 indicates satisfactory elongation at break and tensile strength.
similar resources
بررسی اثر نسبت nco/oh بر خواص مکانیکی ماده منفجره پلاستیکی pbxn-۱۰۹(علمی-پژوهشی)
هدف این مقاله بهبود خاصیت ازدیاد طول در شکست ماده منفجره پلاستیکی pbxn-109 می باشد. با توجه به تاثیر نسبت گروه های ایزوسیانات به هیدروکسیل (r=nco/oh) در تعیین خواص مکانیکی مواد منفجره پلاستیکی، در این تحقیق نمونه های مختلف با نسبت گروه های ایزوسیانات به هیدروکسیل برابر 1، 95/0، 85/0، 75/0 و 65/0 تهیه شده و تحت آزمون های کشش و سختی قرار گرفتند. نتایج آزمایشات نشان دادند که در نسبت 65/0r= و کمتر،...
full textاثر نرم‌کننده‌های مختلف بر خواص ماده منفجره زیرآبی PBXN-111
PBXN-111 is a common plastic bonded explosive has been widely used in warhead section of several navy weapons. This charge is based on HTPB resin and prepared with cast-cure method. Isodecyl pelargonate (IDP) as plasticizer is used in PBXN-111 formulation. Considering limitations to prepare IDP, in this research the effect of replacement of dioctyl adipate (DOA) and dioctyl sebacate (DOS) inste...
full textپارامترهای تجزیه حرارتی ماده منفجره پلاستیکی PBXN-111
PBXN-111 is a cast cured underwater explosive containing RDX, ammonium perchlorate, aluminium powder and HTPB binder. In this research, the kinetics and thermodynamic properties of thermal decomposition of this PBX investigated by Kissinger and Flynn-Wall-Ozawa (FWO) methods based on differential scanning calorimetry under non-isothermal condition with heating rate of 5, 10, 15 and 20 °C/mi...
full textجایگزینی بایندر پرانرژی ماده منفجره زیرآبی PBXN-103 با پلی‌گلیسیدیل نیترات
Plastic bonded explosive PBXN-103 as an underwater charge based on energetic binder system uses in warhead section of several navy weapons. Metriol trinitrate (MTN), triethylene glycol dinitrate (TEGDN) and pelletized nitrocellulose are basic ingredients of binder system in PBXN-103 formulation. In this research the effects of applying accessible Poly glycidyl nitrate (PGN) as binder, were inv...
full textبررسی اثر نوع ماده پرکننده و کاربرد ماده کف زا بر خواص فیزیکی و مکانیکی چندسازه چوب پلاستیک
در این تحقیق امکان ساخت تختههای چوب پلاستیک متخلخل (Wood Plastic Composites Foam) با استفاده از روش قالب‌گیری تزریقی و همچنین اثر نوع ماده لیگنوسلولزی بر خواص کاربردی این چندسازهها مورد بررسی قرار گرفت. تختههای چندسازه چوب پلاستیک به ابعاد 2/3×105×105 میلیمتر از خاک اره چوب صنوبر و پسماندهای حاصل از ساقه سویا با پلیاتیلن سنگین (HDPE) ساخته شدند. همچنین برای متخلخل کردن چند سازههای چوب پلا...
full textماده منفجره TKX-50
Increasing the explosion power simultaneously reduction of explosive sensitivity caused to preparing new species of explosives. One of the considerable compounds in this field is dihydroxyl ammonium 5,5′-bistetrazole-1,1′-diolate (TKX-50). Evaluation of explosion properties of this material shows that its explosion efficiency is equal with CL-20. TKX-50 is compatible with most of th...
full textMy Resources
Journal title
volume 9 issue 2
pages 35- 41
publication date 2014-10
By following a journal you will be notified via email when a new issue of this journal is published.
No Keywords
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023