اثر تعداد چرخه‌های مکانیکی بر استحکام باند ریزکششی ادهزیوهای توتال اچ به عاج

Authors

  • حاتمی حاجی آقا, معصومه
  • دانش کاظمی, علیرضا
  • داوری, عبدالرحیم
  • موسوی نسب, مجید
Abstract:

Introduction: Today load cycling is used for similarity of invitro and invivo studies, though different results were reported in different studies. Therefore, this study aimed to investigate the effect of load cycling on micro tensile bond strength of two total etch adhesives to dentin. Methods: Enamel of 48 molar teeth were removed to expose the superficial dentin. The teeth were randomly divided into two equal groups, and were restored with Single bond (SB), ExciTE and Synergy composite. Then the teeth of each group were divided to 4 equal sub groups. Moreover, load cycling of 0, 50, 100, 200 k load cycle with 50 newton load was used. In each sub group, 12 hour glass slabs with 1mm2 thickness were made. Then the samples were loaded by Dartec testing machine (Model HC/10) with 1 mm/min cross head speed to make the fracture occur. Data were analyzed by ANOVA, t-test, Bonferroni tests. Results: The most micro tensile bond strength belonged to ExciTE without load cycling and lowest refered to SB with 200 k. There was a significant difference between the groups (p ExciTE= 0.0001, p SB = 0.001). Micro tensile bond strength in SB group was significantly lower than ExciTE (p= 0.001). Moreover, load cycling had negative effect on micro tensile bond strength. Conclusion: By increasing load cycling, micro tensile bond strength of both bondings decreased significantly

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

اثر تعداد چرخه های مکانیکی بر استحکام باند ریزکششی ادهزیوهای توتال اچ به عاج

مقدمه: امروزه برای شبیه تر شدن مطالعات آزمایشگاهی به محیط دهان از چرخه های مکانیکی استفاده می شود، ولی در مطالعات مختلف نتایج متفاوتی به دست آمده است. هدف از این مطالعه بررسی اثر تعداد چرخه های مکانیکی بر روی استحکام باند ریزکششی دو نوع ادهزیو توتال اچ به عاج بود. روش بررسی: مینای 48 دندان مولر حذف شد تا عاج سطحی اکسپوز شود. دندان ها به طور تصادفی به دو گروه مساوی تقسیم شدند و با باندینگ هایsin...

full text

بررسی اثر زمان و دمای تبخیر حلال دو نوع ادهزیوتوتال اچ بر استحکام باند ریزکششی کامپوزیت به عاج

Introduction: Effect of drying time and temperature of solvent evaporation were different in different studies. Therefore, the aim of this study was to investigate the appropriate drying temperature and time of solvent evaporation in the two adhesives of Etch and Rinse. Methods: Seventy-two sound third molars were collected. On the buccal surface of the crown, flat dentinal surfaces were crea...

full text

بررسی اثر استفاده مجدد از میکروبراش بر استحکام باند ریزکششی ادهزیو به عاج

Background and Aims: Re-application of microbrush may affect the micro tensile bond strength of adhesives to dentin. The aim of this study was to evaluate the effect of re-application of microbrushes on the micro tensile bond strength of an adhesive to dentin.Materials and Methods: Thirty freshly extracted molars teeth were collected and enamel of occlusal surface were removed to expose superfi...

full text

مقایسۀ تأثیر کلرهگزیدین بر استحکام باند کششی ادهزیوهای سلف اچ دو مرحله‌ای با فلوراید و بدون فلوراید به عاج

زمینه و هدف: استفاده از کلرهگزیدین برای ضدعفونی سطوح دندانی می‌تواند اثرات منفی باکتری‌های باقیمانده در حفره را کاهش دهد. تحقیق حاضر با هدف تعیین اثرات کلرهگزیدین و نیز اثرات حضور همزمان فلوراید و کلرهگزیدین روی استحکام باند ریز کششی ادهزیو‌های سلف اچ دو مرحله‌ای انجام شده ­است. روش‌ بررسی: 20 دندان مولر انسانی برش­خورده پس از اکسپوز عاج تهیه و در 4 گ...

full text

بررسی اثر زمان خشک کردن با هوا بر استحکام باند ریزکششی یک ادهزیو به عاج

Background and Aims: Today, use of adhesive systems is the most common materials in restorative dental procedures. The aim of this study was to evaluate the effect of different air-drying periods on the microtensile bond strength of composite to dentin using adhesive. Materials and Methods: 15 sound molar teeth were selected. The an occlusal surfaces of teeth were removed with silicon carbide d...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 21  issue 2

pages  161- 171

publication date 2013-06

By following a journal you will be notified via email when a new issue of this journal is published.

Keywords

No Keywords

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023