اثر افزودن نانوذرات Gd2O3 بر خواص ساختاری و ابررسانایی YBa2Cu3O7

Authors

  • عربی, هادی دانشگاه فردوسی
  • مؤمنی لاریمی, زبیده دانشگاه بیرجند
  • امیرآبادی‌زاده, احمد دانشگاه بیرجند
  • حسین زاده, سمیه دانشگاه بیرجند
  • کمیلی, مجتبی دانشگاه بیرجند
Abstract:

Gd2O3 nanoparticles were synthesized for the first time by sol-gel combustion method and YBCO high temperature superconductor by sol-gel method. X-ray powder diffraction pattern of the nanoparticles and prepared superconductor showed single phase by both methods. The average size of Gd2O3 nanoparticles, according to the Scherrer formula, computed 29 nm, which is consistent with the results obtained from the TEM images. The nanoparticles with two weight perecent of 0.05 and 0.1 were added to YBCO superconductor. The morphology, structure and superconducting properties investigated by scanning electron microscopy, X-ray diffraction and AC susceptibility in product powders respectively. Rietveld refinements from X-ray diffraction data and results of characteristic showed that both Gd2O3 and YBCO phases coexisted in the products and critical temperature of superconductor decreased with increasing additive content.

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

اثر افزودن نانوذرات gd۲o۳ بر خواص ساختاری و ابررسانایی yba۲cu۳o۷

نانوذرات gd2o3 برای اولین بار، به روش سل ژل احتراقی و ابررسانای دمای بالای yba2cu3o7 به روش سل ژل تهیه شدند. الگوی پرتو ایکس از نانوذرات و ابررسانای تهیه شده، تک فاز بودن هر دو را تایید کرد. اندازه متوسط نانوذرات gd2o3 با استفاده از رابطه­ی شرر 29 نانومتر برآورد شد، که با نتایج حاصل از تصاویر tem، هم خوانی دارد. نانوذرات با دو درصد وزنی 05/0 و 1/0 به نمونه ابررسانای ybco اضافه شد. ریخت شناسی، خ...

full text

اثر دمای بازپخت بر خواص اپتیکی و ساختاری نانوذرات ZnS

ZnS nanoparticles were synthesized by chemical precipitation method. As-prepared ZnS nanoparticles were found to be stabilized in the form of cubic phase. Cubic to hexagonal structural transformation was studied using X-ray diffraction (XRD). The effect of annealing temperature (100-700 ) on the band gap, particle size, and structural phase was investigated. Photoluminescence studies indicated ...

full text

خواص ساختاری و ابررسانایی نمونه‌های (YBa2Cu3-xMxOy (M=Ag, Al

  Samples of YBa2Cu3-xAgxOy with x=0, 0.1, 0.15, 0.2, 0.3 and samples of YBa2Cu3-xAlxOy with x=0, 0.01, 0.02, 0.03 and 0.045 are prepared by the sol-gel method. Structural and superconducting properties of samples are studied by electrical resistivity (R-T), X-ray diffraction (XRD) and scanning electron microscopy (SEM). All the samples show transition to superconducting state and the transitio...

full text

اثر افزودن اسپینل ZnFe2O4روی خواص فوتوکاتالیستی نانوذرات ZnO

در این پژوهش فعالیت فوتوکاتالیستی ZnO با باند گپ eV 2/3 و کامپوزیت آن با نیمه‌هادی ZnFe2O4 با باند گپ eV 9/1 بررسی شده است. همچنین تاثیر افزایش درصد ZnFe2O4 به ZnO روی فعالیت فوتوکاتالیستی نانوکامپوزیت ZnO-ZnFe2O4 مورد بررسی قرار گرفته است. از روش میکروامولسیون معکوس به ‌عنوان روشی جدید در سنتز نانوذرات استفاده شده و همچنین مقادیر ZnO-(10, 30, 50%) ZnFe2O4 از این نانوکامپوزیت برای بررسی سنتز شد...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 21  issue 4

pages  757- 764

publication date 2014-01

By following a journal you will be notified via email when a new issue of this journal is published.

Keywords

No Keywords

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023