observation of stacking fault tetrahedral in twip steel
Authors
abstract
low stacking fault energy face centered cubic (fcc) materials contain characteristic defect structures. stackingfault tetrahedral are one of those rare structures that occur under special experimental conditions. for the first time,stacking fault tetrahedral were observed in fe-30mn-3al-3si twinning induced plasticity (twip) steel. theirpresence resulted from a quenching heat treatment.
similar resources
Observation of Stacking Fault Tetrahedral in TWIP Steel
Low stacking fault energy face centered cubic (FCC) materials contain characteristic defect structures. Stacking fault tetrahedral are one of those rare structures that occur under special experimental conditions. For the first time, stacking fault tetrahedral were observed in Fe-30Mn-3Al-3Si twinning induced plasticity (TWIP) steel. Their presence resulted from a quenching heat treatment.
full textStacking Fault Energy and Microstructural Insight into the Dynamic Deformation of High-Manganese TRIP and TWIP Steels
The dynamic behavior of three high manganese steels with very different stacking faultenergy (SFE) values (4-30 mJ/m2) were studied using high strain rate torsional tests. The hotrolledmicrostructure of the steel with the lowest SFE of 4 mJ/m2 consisted of a duplex mixture ofaustenite and ε-martensite, but those of the other two steels were fully austenitic. The deformedmicrostructures were stu...
full textMechanical behaviour of TWIP steel under shear loading
Twinning induced plasticity steels (TWIP) are very good candidate for automotive industry applications because they potentially offer large energy absorption before failure due to their exceptional strain hardening capability and high strength. However, their behaviour is drastically influenced by the loading conditions. In this work, the mechanical behaviour of a TWIP steel sheet sample was in...
full textTwin-Induced Plasticity of an ECAP-Processed TWIP Steel
The TWIP steels show high strain hardening rates with high ductility which results in high ultimate tensile strength. This makes their processing by equal channel angular pressing very difficult. Up to now, this has only been achieved at warm temperatures (above 200 C). In this paper, a FeMnCAl TWIP steel has been processed at room temperature and the resulted microstructure and mechanical prop...
full textInfluence of High Strain Rates on the Mechanical Behavior of High-Manganese Steels
In this work, dynamic mechanical properties of three high-manganese steels with TRIP/TWIP or fully TWIP characteristics are studied. High strain rate experiments in the range of true strain rates between ~500 and 1800 /s are conducted using a dynamic torsional testing setup. All the three steels show a positive strain rate sensitivity in the intermediate range of strain rates (up to 500 /s). Bu...
full textDeformation Microstructure and Texture in a Cold-Rolled Austenitic Steel with Low Stacking-Fault Energy
Deformation microstructure and texture in a cold-rolled austenitic steel 310S with low stacking fault energy (SFE) have been investigated by SEM and TEM. When 310S plates were rolled by 95% in thickness reduction, a remarkable development of the brass-type preferred orientation was confirmed by X-ray diffraction. SEM observations of the specimens with such texture exhibited a layered structure ...
full textMy Resources
Save resource for easier access later
Journal title:
international journal of iron & steel society of iranPublisher: iron & steel society of iran
ISSN 1735-4145
volume 12
issue 2 2015
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023