synthesis and electrochemical study of nano graphitic mesoporous carbon

Synthesis and Electrochemical Study of Nano Graphitic Mesoporous Carbon

In the present study, a type of graphitic mesoporous carbon (denoted as GMC) is synthesized and its structural properties were characterized by nitrogen physisorption isotherms, transmission electron microscopy and Raman spectroscopy. According to BET and BJH methods, the specific surface area (SBET) and the average pore diameter of GMC are estimated to be 720 m2/g and 3.4 nm, respectively....

Synthesis and Characterization of a Novel Nanoporous Composite Based on Elemental Sulfur and Graphitic Mesoporous Carbon

A novel sulfur nanocomposite was fabricated based on graphitic mesoporous carbon.The graphitic mesoporous carbon was synthesized using sucrose as carbon precursor, nano CaCO3 as a hard template and nickel nitrate as graphitization catalyst. The structural properties of the prepared material were characterized using powder X-Ray Diffraction (XRD), N2-adsorption/de...

synthesis of amido alkylnaphthols using nano-magnetic particles and surfactants

we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.

synthesis and characterization of a novel nanoporous composite based on elemental sulfur and graphitic mesoporous carbon

a novel sulfur nanocomposite was fabricated based on graphitic mesoporous carbon.the graphitic mesoporous carbon was synthesized using sucrose as carbon precursor, nano caco3 as hard template and nickel nitrate as graphitization catalyst. the structural properties of the prepared material were characterized using powder x-ray diffraction (xrd), n2-adsorption/desorption and scanning electron mic...

preparation and characterization of new co-fe and fe-mn nano catalysts using resol phenolic resin and response surface methodology study for fischer-tropsch synthesis

کاتالیزورهای co-fe-resol/sio2و fe-mn-resol/sio2 با استفاده از روش ساده و ارزان قیمت همرسوبی تهیه شدند. از رزین پلیمری resol در فرآیند تهیه کاتالیزور استفاده شد.

Covalent modification of Graphitic Carbon Substrates by Non- Electrochemical Methods