Rapid microwave assisted synthesis of hydroxyapatite
نویسندگان
چکیده
A fast, efficient and novel method of preparation of hydroxyapatite using microwaves has been described.
منابع مشابه
One Step Rapid Synthesis of Nano-Crystalline ZnO by Microwave-Assisted Solution Combustion Method
In this study nano-crystalline ZnO particles were synthesized by microwave-assisted solution combustion method. Zinc nitrate and urea were used as oxidizer and fuel, respectively. The effect of fuel to oxidizer (F/O) ratio on ZnO powder properties was investigated by using different urea/nitrate ratios. X-ray diffractometer, scanning electron microscopy and fourier transform infra-red were used...
متن کاملA Tandem Scalable Microwave-Assisted Williamson Alkyl Aryl Ether Synthesis under Mild Conditions
An efficient tandem synthesis of alkyl aryl ethers, including valuable building blocks of dialdehyde and dinitro groups under microwave irradiation and solvent free conditions on potassium carbonate as a mild solid base has been developed. A series of alkyl aryl ethers were obtained from alcohols in excellent yields by following the Williamson ether synthesis protocol under practical mild condi...
متن کاملUsing Taguchi Experimental Design to Develop an Optimized Synthesis Procedure of Sodalite Prepared by Microwave and Ultrasonic Assisted Aging
Perlite or pearl stone is a natural glass which has formed by rapid cooling of viscous lava or magma. Perlite is mainly composed of silica, aluminum, potassium and sodium. In this experiment, perlite was used as a low-cost source of Si and Al to synthesis of sodalite zeolite using the alkaline hydrothermal treatment. A statistical Taguchi design of experiments was employed to evaluate the effec...
متن کاملMicrowave-assisted rapid synthesis of Co3O4 nanorods from CoC2O4.2H2O nanorods and its application in photocatalytic degradation of methylene blue under visible light irradiation
In this work, Co3O4 nanorods were successfully prepared by microwave-assisted solid state decomposition of rod-like CoC2O4.2H2O precursor within a very short reaction time (6 min) without the use of a solvent/surfactant and complicated equipment. The as-obtained Co3O4 nanorods were fully characterized by X-ray diffract...
متن کاملMicrowave-assisted rapid synthesis of Co3O4 nanorods from CoC2O4.2H2O nanorods and its application in photocatalytic degradation of methylene blue under visible light irradiation
In this work, Co3O4 nanorods were successfully prepared by microwave-assisted solid state decomposition of rod-like CoC2O4.2H2O precursor within a very short reaction time (6 min) without the use of a solvent/surfactant and complicated equipment. The as-obtained Co3O4 nanorods were fully characterized by X-ray diffract...
متن کامل