Elastic behavior and pressure-induced structural evolution of nepheline: Implications for the nature of the modulated superstructure

The elastic behavior and the pressure-induced structural evolution of a natural nepheline (K0.54 Na3.24Ca0.03Al4Si4O16) were investigated by in-situ single-crystal X-ray diffraction up to 7.5 GPa with a diamond anvil cell under hydrostatic conditions. As observed in previous studies, at room conditions the diffraction pattern of nepheline includes satellite reß ections, whereas the structure reÞ nement to the Bragg reß ections conÞ rms that the O1 site is displaced from the triad at (2/3, 1/3, z). The reß ection conditions conÞ rm that the space group of the average structure of nepheline remains as P63 throughout the pressure range investigated, and no signiÞ cant compression of the T-O bonds was measured up to 7.5 GPa. As pressure was increased to around 1 GPa the integrated intensities of the satellites decreased slightly, and at 1.8 GPa no signiÞ cant intensity of the satellites was detected. Over the same pressure range the O1 site moved toward the triad and thus the tilts of the T1 and T2 tetrahedra decreased. The presence of the subsidiary non-Bragg reß ections is therefore related to the split of the O1 site. When the satellites disappear at pressures above 2 GPa, the O1 site is on the triad at (2/3, 1/3, z), corresponding to a straight T1-O1-T2 bond. Below 2 GPa the structure responds to increased pressure by tilting of all four tetrahedra and above 2 GPa by tilting of the T3 and T4 tetrahedra alone. The change in compression mechanism arising from the changes in the O1 position is associated with changes in the compression of the unit-cell axes and the unit-cell volume. The volume can be described by fourth-order Birch-Murnaghan equation-of-state with parameters V0 = 723.57(4) Å3, KT0 = 47.32(26) GPa, K' = 2.77(24), and K'' = 0.758(79) GPa–1. The elastic behavior along the aand c-axis can be described with a “linearized” fourth-order Birch-Murnaghan equations-of-state, with the following reÞ ned parameters: a0 = 9.9911(2) Å, KT0(a) = 43.1(3) GPa, K'(a) = 2.5(3), and K''(a) = 0.68(8) GPa–1 for the a-axis and c0 = 8.3700(1) Å, KT0(c) = 58.6(3) GPa, K'(c) = 4.0(3), and K''(c) = 0.85(11) GPa–1 for the c-axis. The pressure-induced structural evolution in nepheline up to 7.5 GPa appears to be completely reversible. The recovery of the modulation upon complete pressure release points to the framework of nepheline having an instability corresponding to a rigid-unit mode with a wave vector corresponding to the observed positions of the satellite reß ections.