Resistance to cleavage cracking and subsequent shearing of high-angle grain boundary
نویسندگان
چکیده
In a previous experimental study, it was observed that the break-through process of a cleavage front across a high-angle grain boundary can be highly nonuniform. While the central part of the boundary can be cleaved quite smoothly, the rest parts must be sheared apart. In this paper, the trapping effect of grain boundary shearing is analyzed in considerable detail. Before the shearing is completed, the crack flanks are locally pinned together and a bridging stress must be provided. The bridging stress has a negative contribution to the local stress intensity at the cleavage front segment that penetrates across the grain boundary, and thus the crack growth driving force must be increased. A closed-form equation is derived to relate the overall fracture resistance to the fracture mode through an energy analysis. Published by Elsevier Ltd.
منابع مشابه
Characteristic length scale in cleavage cracking across high-angle grain boundary
The factors that govern cleavage cracking across high-angle grain boundaries are investigated theoretically. According to previous experimental observations, a cleavage front overcomes the resistance of a high-angle grain boundary by first penetrating across it at a number of break-through points (BTP) and then separating apart persistent grain-boundary islands (PGBI). In the current study, thi...
متن کاملModeling of resistance curve of high-angle grain boundary in Fe–3 wt.% Si alloy
When a propagating cleavage front encounters a high-angle grain boundary it first penetrates through the grain boundary stably. With increasing penetration depth the resistance of the grain boundary rises, resulting in the well-known R-curve. When the balance between the rates of the energy release rate and the grain boundary resistance is reached, the crack advance becomes unstable and the gra...
متن کاملEnergy equilibrium of cleavage front transmission across a high-angle grain boundary in a free-standing silicon thin film
In this article, the crack growth driving force and the resistance to cleavage cracking associated with crack front transmission across a high-angle grain boundary in a silicon thin film are analyzed, and a closed-form solution of grain boundary toughness is obtained. It is noticed that the fracture resistance of the grain boundary is a function of the film thickness. This size effect is attrib...
متن کاملNonuniform cleavage cracking across persistent grain boundary
The nonuniform characteristics of cleavage cracking across high-angle grain boundaries are analyzed in considerable detail. To break through a grain boundary, a cleavage front would first penetrate across the boundary at its central part, with the side sections being locally arrested. Such a front behavior causes a strong crack trapping effect and a large increase in required crack growth drivi...
متن کاملCrack Front Penetration in Transgranular Cleavage Cracking in an Iron–silicon Alloy
Based on the analysis of the crack trapping effect of cleavage ridges and penetration of crack front segments in an iron–silicon alloy, the distance between break-through points along a high-angle grain boundary is investigated. If the break-through points are close to each other, the crack trapping effect is dominant; otherwise, the grain boundary separation in break-through windows governs th...