INVESTIGATION OF THE MECHANICAL, CORROSION PROPERTIES AND WEAR BEHAVIOUR OF ELECTROLESS Ni-P PLATED MILD STEEL
نویسنده
چکیده
In the present study the mild steel (MS) specimens were coated with Nickel-Phosphorus (Ni-P) using acrylic bath. Heat treatment was carried out on specimens under different temperatures and time periods in an inert atmosphere. The various mechanical and tribological tests were performed on specimens. Using weight loss method, the corrosion nature of the samples under different environments was also studied. The results show that there was significant effect in mechanical and chemical properties of the plated specimens. The properties of the heat treated specimens increased significantly with modest loss in fatigue properties.
منابع مشابه
Properties of Electroless Nickel - Phosphorus PPF Deposits after Crystallization
t is well recognized that electroless I.' nickel-phosphorus offers excellent deposition characteristics, such as uniform coverage, freedom from porosity, hardness, corrosion resistance, solderability, braze and weldability, wear resistance and lubricity.' Interest in the properties of electroless nickel has grown in recent years, leading to the development of wide-ranging applications, a compre...
متن کاملSTUDY OF CHARACTERIZATION AND CORROSION RESISTANCE OF NIP/NANO-DIAMOND ELECTROLESS COMPOSITE DEPOSITION
Ni-P Electroless coatings provide appropriate resistance to wear and corrosion. Co-deposition of particles between layers can improve their properties, especially general corrosion and erosion-corrosion behavior by means of nano diamond as reinforcing particles. In this study Ni-P/nano diamond composite deposition were deposited on steel substrate. Structure of the coatings and corrosion r...
متن کاملTiO2 nano-particle effect on the chemical and physical properties of Ni-P-TiO2 nanocomposite electroless coatings
TiO2 nano-particles were used in electroless plating bath to obtain Ni/P/nano-composite coatings. The coatings were heat treated at 200, 400, 600 and 700 oC and their chemical and physical properties were investigated and it was found that 400 oC was the optimum temperature for the heat treatment of the coatings. The micro-hardness test of coatings showed that t...
متن کاملStudying the Effect of the Concentration of PTFE Nanoparticles on the Tribological Behavior of Ni-P-PTFE Composite Coatings
In the past 30 years, electroless nickel (EN) plating has grown to such proportions that these coatings and their applications are now found underground, in outer space, and in a myriad of areas in between. Moreover, in order to further improve the mechanical and tribological properties of the nickel-phosphorous (Ni-P) coatings, Ni-P/PTFE composite coatings can be obtained, which provides even ...
متن کاملCORROSION BEHAVIOR OF ELECTROLESS Ni-P/NANOZnO COATINGS
Abstract:Electroless Nickel-phosphorus (EN) coatings provide high performance in various industrial fields due to their unique properties such as excellent corrosion and wear resistance. This paper aims to study the effect of ZnO nano-particles addition on corrosion behavior of EN coatings. Various amounts of ZnO nano-particles with average diameter of 50 nm were added to hypophosphite reduced ...
متن کامل