From the Cover: Nanoscale waviness of low-angle grain boundaries
نویسندگان
چکیده
www.pnas.org/cgi/content/full/101/52/17936#otherarticles This article has been cited by other articles: E-mail Alerts . click here at the top right corner of the article or Receive free email alerts when new articles cite this article sign up in the box Rights & Permissions www.pnas.org/misc/rightperm.shtml To reproduce this article in part (figures, tables) or in entirety, see: Reprints www.pnas.org/misc/reprints.shtml To order reprints, see:
منابع مشابه
Microstructural evolution of 304 austenitic stainless steel in friction stir welding process
Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...
متن کاملMicrostructural evolution of 304 austenitic stainless steel in friction stir welding process
Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...
متن کاملAtomic-scale quantification of grain boundary segregation in nanocrystalline material.
Grain boundary segregation leads to nanoscale chemical variations that can alter a material's performance by orders of magnitude (e.g., embrittlement). To understand this phenomenon, a large number of grain boundaries must be characterized in terms of both their five crystallographic interface parameters and their atomic-scale chemical composition. We demonstrate how this can be achieved using ...
متن کاملTransition between Low and High Angle Grain Boundaries
Institut für Metallkunde und Metallphysik, RWTH Aachen, 52056 Aachen, Germany Carnegie Mellon University, Pittsburgh PA 15213, USA Abstract The migration of planar, symmetric tilt grain boundaries with different tilt axes was investigated. The driving force for the grain boundary migration was due to an external mechanical stress field. Low as well as high angle grain boundaries can move under ...
متن کاملDirect observation of individual dislocation interaction processes with grain boundaries
In deformation processes, the presence of grain boundaries has a crucial influence on dislocation behavior; these boundaries drastically change the mechanical properties of polycrystalline materials. It has been considered that grain boundaries act as effective barriers for dislocation glide, but the origin of this barrier-like behavior has been a matter of conjecture for many years. We directl...
متن کامل