Starch graft poly(methyl acrylate) loose-fill foam: preparation, properties and degradation.
نویسندگان
چکیده
Starch graft poly(methyl acrylate) (S-g-PMA) was prepared by ceric ion initiation of methyl acrylate in an aqueous corn starch slurry (prime starch) which maximized the accessibility of the starch for graft polymerization. A new ceric ion reaction sequence was established as starch-initiator-methyl acrylate followed by addition of a small amount of ceric ion solution when the graft polymerization was almost complete to quench the reaction. As a result of this improved procedure, no unreacted methyl acrylate monomer remained, and thus, essentially no ungrafted poly(methyl acrylate) homopolymer was formed in the final grafted product. Quantities of the high purity S-g-PMA so prepared in pilot scale were converted to resin pellets and loose-fill foam by single screw and twin screw extrusion. The use of prime starch significantly improved the physical properties of the final loose-fill foam, in comparison to foam produced from regular dry corn starch. The S-g-PMA loose-fill foam had compressive strength and resiliency comparable to expanded polystyrene but higher bulk density. The S-g-PMA loose-fill foam also had better moisture and water resistance than other competitive starch-based materials. Studies indicated that the starch portion in S-g-PMA loose-fill foam biodegraded rapidly, whereas poly(methyl acrylate) remained relatively stable under natural environmental conditions.
منابع مشابه
Effects of molecular structure of acrylates on sizing performance of allyl grafted starch
In order to improve the performance of allyl starch-g-poly(acrylic acid-co-acrylate) sizes, effect of molecular structure of the acrylate monomers grafted onto allyl starch has been studied. A series of acrylates including methyl acrylate (MA), ethyl acrylate (EA), butyl acrylate (BA) and 2-ethylhexyl acrylate (EHA) have been grafted onto allyl starch with the same degree of substitution throug...
متن کاملGraft Polymerization of Vinyl Acetate onto Starch. Saponification to Starch-g-Poly(vinyl Alcohol)
Graft polymerizations of vinyl acetate onto granular corn starch were initiated by cobalt-60 irradiation of starch-monomer-water mixtures. and ungrafted poly(vinyl acetate) was separated from the graft copolymer by benzene extraction. Conversions of monomer to polymer were quantitative at a radiation dose of 1.0 IvIrad. However, over half of the polymer was present as ungrafted poly(vinyl aceta...
متن کاملEffect of alkyl group substituents on the thermal and enzymatic degradation of poly (n-alkyl acrylates)
Effect of alkyl group substituents on the thermal and enzymatic degradation of poly (n-alkyl acrylates) J. P. Mahalik and Giridhar Madras∗ Department of Chemical Engineering, Indian Institute of Science, Bangalore-12 Abstract The effect of alkyl group substituents on the thermal degradation kinetics of poly (n-alkyl acrylate) was investigated in pyrolysis and in solution. The activation energie...
متن کاملPreparation and Surface Modification of Non-porous Micron-sized Magnetic Poly(methyl acrylate) Microspheres
Micron-sized magnetic poly (methyl acrylate) (mPMA) microspheres were prepared by a novel modified suspension polymerization method. mPMA microspheres were highly functionalized by the ammonolysis reaction with ethylenediamine to yield abundant amino groups (-NH2) on the surface. The morphology, magnetic property and surface functionality of the magnetic microspheres were examined by SEM, VSM a...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Biomacromolecules
دوره 5 1 شماره
صفحات -
تاریخ انتشار 2004