Influence of post-treatment operations on structural properties and photocatalytic activity of octahedral anatase titania particles prepared by an ultrasonication-hydrothermal reaction.

The influence of changes in structural and physical properties on the photocatalytic activity of octahedral anatase particles (OAPs), exposing eight equivalent {101} facets, caused by calcination (2 h) in air or grinding (1 h) in an agate mortar was studied with samples prepared by ultrasonication (US; 1 h)-hydrothermal reaction (HT; 24 h, 433 K). Calcination in air at temperatures up to 1173 K induced particle shape changes, evaluated by aspect ratio (AR; d001/d101 = depth vertical to anatase {001} and {101} facets estimated by the Scherrer equation with data obtained from X-ray diffraction (XRD) patterns) and content of OAP and semi-OAP particles, without transformation into rutile. AR and OAP content, as well as specific surface area (SSA), were almost unchanged by calcination at temperatures up to 673 K and were then decreased by elevating the calcination temperature, suggesting that calcination at a higher temperature caused dull-edging and particle sintering, the latter also being supported by the analysis of particle size using XRD patterns and scanning electron microscopic (SEM) images. Time-resolved microwave conductivity (TRMC) showed that the maximum signal intensity (Imax), corresponding to a product of charge-carrier density and mobility, and signal-decay rate, presumably corresponding to reactivity of charge carriers, were increased with increase in AR, suggesting higher photocatalytic activity of OAPs than that of dull-edged particles. Grinding also decreased the AR, indicating the formation of dull-edged particles. The original non-treated samples showed activities in the oxidative decomposition of acetic acid (CO2 system) and dehydrogenation of methanol (H2 system) comparable to and lower than those of a commercial anatase titania (Showa Denko Ceramics FP-6), respectively. The activities of calcined and ground samples for the CO2 system and H2 system showed almost linear relations with AR and Imax, respectively, suggesting that those activities may depend on different properties.