Industrial application of Instrumented DWTT in evaluating material resistance to ductile fracture for modern pipeline steels
نویسندگان
چکیده
CTOAC of typical X70, X80 and X90 pipeline steels plates were evaluated by using energy based regression method upon their single specimen. Clear difference in the material resistance to ductile cracking could be distinguished by the values of CTOAC and their characteristic fracture surface. The region of stable cracking on the fracture surface could be identified from the dynamic crack extension curve, with the help of key-curve method. In the meanwhile, the crucial material based parameter required by many other CTOAC algorithm, (A∗σf) of present X70, X80 and X90 plates were experimentally determined, also proving the validity of theoretical geometric factor A∗ to be 0.30–0.34, close to the commonly cited constant of 1/3.
منابع مشابه
Investigation of Ductile Fracture Arrest of High Strength Steels for Gas Pipeline Application
The ductile fracture arrest may present supplementary requirement for selection of base material for most demanding steel welded structures. The most representative one with such requirement are gas pipelines. Therefore to ensure that the pipeline materials has adequate toughness to arrest a ductile fracture, the pipe material must be designed and tested in accordance with the specific procedur...
متن کاملAdvanced Bearing and Gear Steels for Wind Turbine Applications
There is an urgent need for more durable and cost-effective bearing and gear steels for wind turbine applications; yet we are still using traditional steels such as 8620 and 52100 steels, which are inexpensive and have high strength. However, higher corrosion resistance is required for marine application of wind turbines. Our research group developed under NSF funding a series of high strength ...
متن کاملDamage Behavior in Modern Automotive High Strength Dual Phase Steels During Uniaxial Tensile Deformation
In the present research, damage mechanisms during room temperature uniaxial tensile testing of two different modern high strength dual phase steels,DP780 and DP980, were studied. Detailed microstructural characterization of the strained and sectioned samples was performed by scanning electron microscopy (SEM). The results revealed that interface decohesion, especially at the triple junctions of...
متن کاملDuctile Failure in High Strength Steel Sheets
Developments in computer-aided engineering and the rapid growth of computational power have made simulation-driven process and product development efficient and useful since it enables detailed evaluation of product designs and their manufacturing processes. In the context of a sheet metal component, it is vital to predict possible failure both during its forming process and its subsequent usag...
متن کاملThe Recommend of Filler Metal to Increasing the Corrosion Resistance of Gas Pipeline
The high strength carbon steels such as API X65 is widely used to build the pipelines. In this study, the corrosion behavior welds region of the gas pipeline was studied. For this purpose, Shield Metal Arc Welding (SMAW) was used to evaluate the proposed method. The welding processes were performed with E6010, E6013, and ER70S-6 electrodes as filler metal and welding carried out in 3 passes by ...
متن کامل