Gd-doping of HfO2
نویسندگان
چکیده
An increase in the density of states between the oxygen 2p bands and the Fermi level is seen with increasing Gd concentrations. In addition, for the Gd-doped HfO2 films, the Gd 4f photoexcitation peak at 5.5 eV below the valence band maximum was identified using resonant photoemission. Electrical measurements show pronounced rectification properties for lightly-doped Gd:HfO2 films on p-Si and for heavily-doped Gd:HfO2 films on n-Si, suggesting a crossover from n-type to p-type behavior with increasing doping level. In addition, there is an increase in the reverse bias current with neutron irradiation.
منابع مشابه
اثر آلایش عناصر خاکی نادر سبک در ابررساناهای دمای بالای 123
We have studied the structural and electrical properties of Gd(Ba2-xLax)Cu3O7+δ [Gd(BaLa)123], Gd(Ba2-xNdx)Cu3O7+δ [Gd(BaNd)123], and Nd(Ba2-xPrx)Cu3O7+δ [Nd(BaPr)123] compounds with 0.0≤x≤0.8 prepared by the standard solid-state reaction. The XRD patterns show that all of the samples with x≤0.5 are isosructure 123 phase, but in Gd(BaNd)123 and Nd(BaPr)123 there are several impurity peaks in...
متن کاملOptimization of the 3 m TGM beamline, at CAMD, for constant initial state spectroscopy
The 3 m toroidal grating monochromator (TGM) VUV beamline at CAMD/LSU was realigned to achieve better illumination of the monochromator gratings with the goal of substantially increasing the fl ux at the higher photon energies. This is partly accomplished through a tilting of the monochromator (by about of 13.5°), with respect to the plane defi ned by the synchrotron, providing a smaller grazin...
متن کاملخواص ساختاری، الکترونی و دینامیک شار ابررسانای Gd (Ba2-x) Cu3O7+δ
The Gd(Ba2-xPrx)Cu3O single phase polycrystalline samples with 0.00 ≤ x ≤ 1.00 were investigated for structural, electronic and flux dynamic properties. An unusual hump on the resistivity vs. temperature curve of the samples has been observed for particular values of Pr doping. We have found that the Ba atom substitution at the rare earth site could lead to superconductivity in some parts of ...
متن کاملروتنوکوپراتها: میدان رقابت ابررسانایی و مغناطیس
We have compared the structural, electrical, and magnetic properties of Ru(Gd1.5-xPrx)Ce0.5Sr2Cu2O10-δ (Pr/Gd samples) with x = 0.0, 0.01, 0.03, 0.033, 0.035, 0.04, 0.05, 0.06, 0.1 and RuGd1.5(Ce0.5-xPrx)Sr2Cu2O10-δ (Pr/Ce samples) with x = 0.0, 0.01, 0.03, 0.05, 0.08, 0.1, 0.15, 0.2 prepared by the standard solid-state reaction technique with RuGd1.5(GdxCe0.5-x) Sr2Cu2O10-δ (Gd/Ce samples) wi...
متن کاملBi-functional NaLuF4:Gd3+/Yb3+/Er3+ nanocrystals: hydrothermal synthesis, optical and magnetic properties
Magnetic-fluorescent lanthanide doped sodium lutetium fluoride (NaLuF4:Yb3+/Er3+/Gd3+) nanocrystals were synthesized via facile hydrothermal method by varying concentration of Gd3+. Powder X-ray powder diffraction (PXRD), scanning electron microscopy (SEM),transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS), p...
متن کامل